Magnesium hydride films deposited on flexible substrates: Structure, morphology and hydrogen sorption properties

Huy Le-Quoc,Marie Coste,Ana Lacoste,L. Laversenne

DOI: https://doi.org/10.1016/j.jallcom.2023.170272

2023-11-02

Abstract:1.8 micrometer-thick magnesium hydride films were synthesized in a single-step process by reactive plasma-assisted sputtering. The MgH2 thin films, which were deposited on two types of flexible surfaces (namely graphite and polyimide foils) were found to adhere on both substrates. In all cases, XRD analysis revealed an as-deposited thin film consisting of alpha-MgH2, a tetragonal, rutile-type crystal structure (space group \#136). The hydrogen sorption capacities of the uncapped films were studied over successive desorption/absorption cycles performed at 350 {\textdegree}C. The first desorption always shows a slow kinetics that can be explained by a superficial oxidation of the films. However, once the passivating layer is removed, the following dehydrogenations occur faster. Multiple cycling of the film deposited on polyimide resulted in delamination of the film and its conversion into loose powder. As for MgH2 deposited on the flexible graphite substrate, a fully reversible capacity was observed over 28 cycles with no delamination of the film. Upon cycling, the microstructure of the film has evolved from homogeneous fibrous to an untextured morphology with a higher degree of crystallinity.

Applied Physics,Materials Science

What problem does this paper attempt to address?

### Problems Addressed by the Paper

The paper primarily explores the methods and performance of depositing magnesium hydride (MgH₂) thin films on flexible substrates. Specifically, the research team successfully prepared MgH₂ thin films with a thickness of approximately 1.8 micrometers on polyimide foil and graphite sheets using reactive plasma-assisted sputtering technology. The main issues addressed by the paper are as follows:

1. **Deposition Methods and Performance**:
- Researchers used a single-step reactive plasma-assisted sputtering technology (PAPVD) to successfully deposit MgH₂ thin films on flexible substrates.
- The performance of these films in hydrogen absorption and desorption cycles, particularly at 350°C, was investigated.

2. **Structural and Morphological Analysis**:
- Detailed structural and morphological analyses of the films were conducted using X-ray diffraction (XRD) and scanning electron microscopy (SEM).
- The results showed that the deposited films had good crystallinity, and the films on graphite substrates exhibited preferred crystal orientation.

3. **Hydrogen Absorption and Desorption Capacity**:
- The capacity changes of the films during multiple hydrogen absorption and desorption cycles were studied.
- It was found that the films had a surface oxide layer in the initial few cycles, but once removed, the subsequent dehydrogenation process significantly accelerated.
- On polyimide substrates, the films showed peeling and pulverization after multiple cycles; whereas on graphite substrates, the films maintained good adhesion even after 28 cycles.

4. **Impact of Different Substrates**:
- The performance differences of the films on polyimide and graphite substrates were compared.
- The low thermal conductivity of the polyimide substrate led to stress generation in the films during hydrogen cycling, causing peeling; whereas the high thermal conductivity of the graphite substrate helped release stress, making the films more stable during cycling.

5. **Application Prospects**:
- The potential of depositing MgH₂ films on flexible substrates for practical applications, especially in portable and wearable devices, was discussed.
- Although the current hydrogen storage capacity is relatively low, researchers believe that by optimizing parameters such as film thickness ratio, it is possible to further improve performance in the future.

In summary, the paper aims to demonstrate a new method for preparing high-performance MgH₂ films on flexible substrates and to explore their potential in hydrogen storage and related applications.