Abstract:Magnesium hydride has been seen as a potential material for solid state hydrogen storage, but the kinetics and thermodynamics obstacles have hindered its development and application. Three-dimensional flower-like TiO2@C and TiO2 were synthesized as the catalyst for MgH2 system and great catalytic activities are acquired in the hydrogen sorption properties. Experiments also show that the flower-like TiO2@C is superior to flower-like TiO2 in improving the hydrogen storage properties of MgH2. The hydrogen desorption onset and peak temperatures of flower-like TiO2 doped MgH2 is reduced to 199.2 degrees C and 245.4 degrees C, while the primitive MgH2 starts to release hydrogen at 294.6 degrees C and the rapid dehydrogenation temperature is even as high as 362.6 degrees C. The onset and peak temperatures of flower-like TiO2@C doped MgH2 are further reduced to 180.3 degrees C and 233.0 degrees C. The flower-like TiO2 @C doped MgH2 composite can release 6.0 wt% hydrogen at 250 degrees C within 7 min, and 4.86 wt% hydrogen at 225 degrees C within 60 min, while flower-like TiO2 doped MgH2 can release 6.0 wt% hydrogen at 250 degrees C within 8 min, and 3.89 wt% hydrogen at 225 degrees C within 60 min. Hydrogen absorption kinetics is also improved dramatically. Moreover, compared with primitive MgH2 and the flower-like TiO2 doped MgH2, the activation energy of flower-like TiO2@C doped MgH2 is significantly decreased to 67.10 kJ/mol. All the improvement of hydrogen sorption properties can be ascribed to the flower-like structure and the two-phase coexistence of TiO2 and amorphous carbon. Such phase composition and unique structure are proved to be the critical factor to improve the hydrogen sorption properties of MgH2, which can be considered as the new prospect for improving the kinetics of light-metal hydrogen storage materials. (C) 2019 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.

Hydrogen-induced optical properties of FC/Pd/Mg films: Roles of grain size and grain boundary

Effects of Amorphous and Nanocrystalline Structures on Hydrogen-Induced Optical Performance of Modulated Mg-Gd Films with Various Composition Fluctuations.

Hydrogen storage and structure variation in Mg/Pd multi-layer film

Improved Hydrogen Storage Properties in Mg-based Thin Films by Tailoring Structures

Hydrogen Absorption–desorption, Optical Transmission Properties and Annealing Effect of Mg Thin Films Prepared by Magnetron Sputtering

Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability

Hydrogen-induced Magnetic and Structural Changes in Pd/Co/Mg Multilayer

Fast Hydrogen-Induced Optical and Electrical Transitions of Mg and Mg-Ni Films with Amorphous Structure

A kinetics study on promising hydrogen storage properties of Mg-based thin films at room temperature.

Microstructures And Hydrogen Desorption Properties Of The Mgh2-Alh3 Composite With Nbf5 Addition

Hydrogen desorption properties of Mg thin films at room temperature

Hydrogen Absorption Kinetics of Mg Thin Films under Mild Conditions

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Superior De/hydrogenation Performances of MgH2 Catalyzed by 3D Flower-Like TiO2@C Nanostructures

Microstructure, Hydrogenation and Optical Behavior of Mg–Ni Multilayer Films Deposited by Magnetron Sputtering

Superior hydrogen absorption and desorption behavior of Mg thin films

Excellent hydrogen sorption kinetics of thick Mg-Pd films under mild conditions by tailoring their structures

Superior Hydrogen Storage and Electrochemical Properties of Mg(x)Ni(100-x)/Pd Films at Room Temperature.

Isothermal hydrogen absorption process of Pd-capped Mg films traced by ion beam techniques and optical methods

Turning optical switching properties of Mg-Y films in electrochemical process by tailoring composition

In-situ Formation of Uniform Mg2Ni Catalyst and Hydrogen Storage Properties of Mg41Ni Alloys with Varied Grain Sizes and Morphologies