Abstract:316 stainless steel (SS) was coated with CoCrFeNiNbx (x: atomic ratio, x = 0, 0.1, 0.2, and 0.3) high entropy alloy coatings (HEACs) by laser cladding (LC). The impacts of Nb content on the phase composition, microstructure, microhardness, wear resistance and corrosion properties of CoCrFeNi based HEACs were examined. Different from the canonical dendritic (DR) - interdendritic (ID) microstructure presented by the other three HEACs, the ID of Nb0.3 HEACs also existed nanoscale Nb-rich Laves phase composed of Nb-Ni and Nb-Co. The inclusion of Nb significantly reduced the average grain size of CoCrFeNi based HEACs from 59.43 mu m to 11.38 mu m. It also greatly diminished the formation of high angle grain boundaries (HAGBs), increasing the percentage of low angle grain boundaries (LAGBs) from 31 % to 61 %. The microhardness of Nb-containing HEACs was significantly promoted due to the solid solution strengthening and fine grain strengthening caused by large size Nb atoms. Affected by Laves phase with high coordination number and space filling ratio and higher proportion of LAGBs, the microhardness of Nb0.3 HEAC was even as high as 530 HV. The increase in Nb concentration also strengthened the HEACs' resistance to wear. Nb0, Nb0.1, Nb0.2, and Nb0.3 HEACs had corresponding specific wear rates of 0.36, 0.32, 0.23, and 0.20 mm3/Nm. Unlike 316 SS, Nb0 and Nb0.1 HEACs, which had both adhesive wear and abrasive wear, Nb0.2 and Nb0.3 HEACs were mainly wear by abrasive wear. The corrosion behavior of CoCrFeNiNbx HEACs in 0.5 M H2SO4 solution was similar to 316 SS, but the corrosion resistance was stronger than 316 SS. Nb0.3 HEAC with the Ecorr of -164 mV and Icorr of 6.40 x 10-7 A/cm2 showed the best acid corrosion resistance, which could be attributed to the stable and dense passivation film on its surface. Distinct from the intergranular corrosion of other coatings, the corrosion of Nb0.3 HEAC mainly occurred in DR, because the FCC phase acted as the anode site in it when FCC and Laves phase co-existed.

Microstructure evolution and characteristics of laser-clad lightweight refractory NbxMo$_{0.5}$Ti$_{1.5}$Ta$_{0.2}$Cr high-entropy alloy

Electrochemical Corrosion Behavior in Sulfuric Acid Solution and Dry Sliding Friction and Wear Properties of Laser-Cladded CoCrFeNiNb High Entropy Alloy Coatings

Microstructure and wear resistance of in-situ TiN/ (Nb, Ti) 5 Si 3 reinforced MoNbTaWTi-based refractory high entropy alloy composite coatings by laser cladding

Microstructure of NbMoTaTiNi Refractory High-Entropy Alloy Coating Fabricated by Ultrasonic Field-Assisted Laser Cladding Process

Evolution in microstructure and tribological behavior of laser cladded MoxNbTiZr high-entropy refractory alloy coatings with varying Mo content

Evolution in Wear and High-Temperature Oxidation Resistance of Laser-Clad AlxMoNbTa Refractory High-Entropy Alloys Coatings with Al Addition Content

Mo20Nb20Co20Cr20(Ti8Al8Si4) Refractory High-Entropy Alloy Coatings Fabricated by Electron Beam Cladding: Microstructure and Wear Resistance

Microstructure and Friction Properties of AlCrTiVNbx High-Entropy Alloys via Annealing Manufactured by Vacuum Arc Melting

Microstructure evolution and performance of TiMoCrW x Ta y refractory high-entropy alloy coatings prepared using laser cladding

Strengthening mechanisms and high-temperature oxidation properties of laser-clad TaNbZrTi refractory high entropy alloy coatings

Investigation into Microstructure, Wear Resistance in Air and NaCl Solution of AlCrCoNiFeCTax High-Entropy Alloy Coatings Fabricated by Laser Cladding

Microstructure and hardness of NbTiZr and NbTaTiZr refractory medium-entropy alloy coatings on Zr alloy by laser cladding

First Principles Calculation of the Influence of Alloying on the Phase Stability, Elasticity, and Thermodynamic Properties of the MoNbTiVX (X = Al/Cr) Refractory High-Entropy Alloy

Microstructure and wear property of WMoTaNb refractory high entropy alloy coating by laser cladding

Lightweight refractory high entropy alloy coating by laser cladding on Ti–6Al–4V surface

Effects of Nb content on the microstructure and properties of CoCrFeMnNiNb x high-entropy alloy coatings by laser cladding

Microstructure and wear behavior of mechanically alloyed powder AlxMo0.5NbFeTiMn2 high entropy alloy coating formed by laser cladding

Enhanced Strength and Ductility of Laser Powder Bed Fused NbMoTaW Refractory High-Entropy Alloy Via Carbon Microalloying

Microstructure and Wear Characteristics of Laser-Clad CoCrFeMnNiNb0.3 High-Entropy Alloy Coating

Microstructure and properties of W0.5Ta0.3MoNbVAlTi1-xZrx high entropy alloy coatings by laser cladding on the surface of 45# steel

Design and Characterization on Microstructure Evolution and Properties of Laser-Cladding Ni1.5CrFeTi2B0.5Mox High-Entropy Alloy Coatings