The Microstructures and Wear Resistance of CoCrFeNi2Mox High-Entropy Alloy Coatings
Liang,Hou,Liu,Xu,Li,Jiang,Cao
DOI: https://doi.org/10.3390/coatings14060760
IF: 3.236
2024-06-16
Coatings
Abstract:The CoCrFeNi2Mox (x = 0, 0.4, 0.5, 1.0, x values in atomic ratio) high-entropy alloy coatings were designed and prepared on the Ti-6Al-4V substrate by laser cladding technology, their microstructures, and dry sliding wear resistance were studied in detail. When x < 0.4, the coatings were mainly composed of BCC solid solution phase, (Ni, Co)Ti2 phase, and α-Ti phase. When x ≥ 0.4, the new σ phase appeared in the coatings. As the Mo content increases from 0 to 1.0, the hardness showed a trend of first increasing and then decreasing, especially when x = 0.5, the coating hardness reached its maximum (882 HV), which was 2.65 times the hardness of the Ti-6Al-4V substrate. The CoCrFeNi2Mox high-entropy alloy coatings significantly improved the wear resistance of Ti-6Al-4V substrate, and with the increase in Mo content, the friction coefficient, widths/depths of worn tracks and wear rates of the coatings showed a trend of first decreasing and then increasing. In particular, when x = 0.5, the CoCrFeNi2Mo0.5 high-entropy alloy coating has the lowest friction coefficient (0.63), widths/depths of worn tracks (width: 803.690 μm; depth: 20.630 μm) and wear rate (5.136 × 10−5 mm3/(N·m)), which is one order of magnitude smaller than that of the substrate (3.694 × 10−4 mm3/(N·m)), demonstrating the best wear resistance. This is mainly because the appropriate proportion of hard α-Ti and σ phases effectively played a supporting role in resisting wear, while the relatively soft and dispersed BCC and (Ni, Co)Ti2 phases could effectively prevent the occurrence of brittle fracture during wear test process.
materials science, multidisciplinary,physics, applied, coatings & films