Microstructure and hardness of NbTiZr and NbTaTiZr refractory medium-entropy alloy coatings on Zr alloy by laser cladding

Haotian Guan,Linjiang Chai,Yueyuan Wang,Kang Xiang,Lu Wu,Hucheng Pan,Mingbo Yang,Changqing Teng,Wei Zhang

DOI: https://doi.org/10.1016/j.apsusc.2021.149338

IF: 6.7

2021-05-01

Applied Surface Science

Abstract:<p>Two refractory medium-entropy alloy (RMEA) coatings (NbTiZr and NbTaTiZr) with BCC solid-solution phase as their main constitutional phase were successfully fabricated on Zr702 alloy by utilizing pulsed laser cladding. Phase constitutions, chemical compositions, crystallographic orientations and hardnesses of the coatings were carefully characterized and analyzed. Results show that both the RMEA coatings correspond to cladding zones (CZs) that are composed of irregular-shaped bulk grains (BCC solid-solution phase) with scattered orientations and 370-380 μm in thickness. The addition of Ta is able to promote grain refinement and produce higher micro strains in the coatings. Theoretical analyses show that the phase constitution in the RMEA coatings is consistent with that predicted according to several thermodynamic or structural parameters. Below the CZs, there exist heat-affected zones (HAZs) consisting of a mixture of bulk α-Zr grains and fine martensite plates. Average thicknesses of the HAZs in both the specimens are 180-190 μm. Hardnesses of the NbTiZr and the NbTaTiZr coatings are 510 ± 22 HV and 550 ± 26 HV, respectively, significantly higher than that of the substrate (196 ± 4 HV). Such high hardnesses are attributed to combined effects of solid-solution strengthening, grain refinement strengthening and increased contents of low angle boundaries.</p>

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films

What problem does this paper attempt to address?

The problems that this paper attempts to solve are as follows: Prepare two refractory medium - entropy alloy (RMEA) coatings (NbTiZr and NbTaTiZr) on zirconium alloy (Zr702) by laser cladding technology to improve the hardness and wear resistance of zirconium alloy. Specifically, the research aims to:

1. **Improve surface properties**: Zirconium and its alloys are widely used in biomedicine, chemistry and nuclear industry due to their excellent biocompatibility, corrosion resistance and low thermal neutron absorption characteristics. However, their low hardness and poor wear resistance limit their applications under frictional conditions. Therefore, the research hopes to optimize the surface properties of zirconium alloy through surface treatment technology (especially pulsed laser cladding technology).

2. **Explore new coating materials**: Niobium (Nb), tantalum (Ta) and titanium (Ti) are selected as alloying elements in the research because these elements can form simple structures when combined with zirconium and exhibit many attractive properties, such as high strength at high temperatures, excellent irradiation and wear resistance, and good biocompatibility. These alloys belong to refractory medium - entropy alloys (RMEA) and have potential application prospects.

3. **Analyze microstructure and mechanical properties**: Through a variety of characterization techniques (such as X - ray diffraction, electron channeling contrast imaging, energy - dispersive spectroscopy analysis and electron back - scatter diffraction, etc.), the microstructure characteristics such as phase composition, chemical composition, crystal orientation and hardness of these two RMEA coatings are studied in detail, and their formation mechanisms are also explored.

4. **Mechanism of increasing hardness**: It is found that the hardness of NbTiZr and NbTaTiZr coatings are 510 ± 22 HV and 550 ± 26 HV respectively, which are significantly higher than that of the matrix material (196 ± 4 HV). This high hardness is attributed to the combined effects of solid - solution strengthening, grain refinement strengthening and an increase in the content of low - angle grain boundaries.

In summary, this research aims to prepare high - performance refractory medium - entropy alloy coatings on zirconium alloy by laser cladding technology, thereby improving its hardness and wear resistance, and providing important references for the preparation and performance optimization of such coatings.