Abstract:Degradation of module encapsulant mechanical characteristics that lead to embrittlement and delamination remains a leading cause of failure in solar modules. Extending module lifetimes beyond 30 years requires advanced predictive modeling that includes the fundamental materials degradation pathways and their dependence on operating temperature, UV, and moisture. We present a time‐dependent multiscale mechanics model based on detailed molecular degradation reaction kinetics that connects the encapsulant bond density and interfacial bond density with its mechanical properties and adhesion energy. Photovoltaic (PV) modules are subjected to environmental stressors (UV exposure, temperature, and humidity) that cause degradation within the encapsulant and its interfaces with adjacent glass and cell substrates. To save experimental time and to enable long‐term assessment with intensive degradation only taking place after many years, the development of predictive models is indispensable. Previous works have modeled the delamination of the ethylene vinyl acetate (EVA) encapsulant/glass and encapsulant/cell interfaces under field aging conditions with fundamental photochemical degradation reactions that lead to molecular scission and loss of interfacial adhesion, characterized by the fracture resistance, Gc. However, these models were fundamentally limited in that the following aspects were not incorporated: (i) molecular crosslinking in the field, (ii) synergistic autocatalytic interactions of degradation mechanisms, (iii) connection between degraded encapsulant structure and its mechanical properties, and (iv) rigorous treatment of the plasticity contribution to Gc with finite element models. Here, we present a time‐dependent multiscale model that addresses these limitations and is applicable to a wide range of encapsulants and interfaces. For the reference EVA encapsulant and its interfaces with the glass and cell, the presented model predicts an initial rise in Gc in the first 3 years of field aging from crosslinking, then a subsequent sharp decline from degradation mechanisms. We used nanoindentation to measure the changes in EVA mechanical properties over exposure time to tune the model parameters. The model predictions of Gc and mechanical properties match with experimental data and show an improvement compared to previous models. The model can even predict switches in failure interfaces, such as the observed EVA/cell to EVA/glass transition. We also conducted a sensitivity analysis study by varying the degradation and crosslinking kinetic parameters to demonstrate their effects on Gc. Model extensions to polyolefin elastomer‐ and silicone‐encapsulants and their interfaces are also demonstrated.

Computational modeling of viscoelastic backsheet materials for photovoltaics

Mechanical Analysis of the Quasi-Static and Dynamic Composite Action in PV Modules with Viscoelastic Encapsulant

Lifetime Evaluation of Photovoltaic Polymeric Backsheets under Ultraviolet Radiation: From Chemical Properties to Mechanical Modeling

Evaluation of Surface Crack Formation in Photovoltaic Backsheets Using Fragmentation and Finite Element Simulations

Material characterization of seven photovoltaic backsheets using seven accelerated test conditions

Degradation analysis of field-exposed photovoltaic modules with non-fluoropolymer-based backsheets

Analyzing photovoltaic module mechanics using composite plate theories and finite element solutions

Predicting encapsulant delamination in photovoltaic modules bridging photochemical reaction kinetics and fracture mechanics

Mathematical model of a solar module for energy yield simulation in photovoltaic systems

Investigation on the Effect of Accumulated Charge-Induced Degradation on Multilayer Photovoltaic Insulating Backsheets Based on Atomic Force Microscopy

Sequential thermomechanical stress and cracking analysis of photovoltaic modules with full and half-cut cells

A physically based visco-hyperelastic constitutive model for soft materials

A Comparison of Emerging Nonfluoropolymer-Based Coextruded PV Backsheets to Industry-Benchmark Technologies

Thermo-mechanical stress modeling and experimental investigation on micro-cracks in tilling ribbon photovoltaic modules during lamination and mechanical load test

A computational framework for rheologically complex thermo-visco-elastic materials

Constitutive Investigation on Viscoelasticity of PolyVinyl Butyral: Experiments Based on Dynamic Mechanical Analysis Method

Thermodynamically consistent modelling of viscoelastic solids under finite strain

Towards validation of combined-accelerated stress testing through failure analysis of polyamide-based photovoltaic backsheets

Modeling the viscoelastic-viscoplastic behavior of glassy polymer membrane with consideration of non-uniform sub-chains in entangled networks

An experimentally validated anisotropic visco-hyperelastic constitutive model for knitted fabric-reinforced elastomer composites

Nanoindentation Reveals Crosslinking Behavior of Solar Encapsulants—The Methodological Advantages over Bulk Methods