Abstract:Since the discovery of superconductivity in mercury at 4 K in 1911, searching for materials with superconductivity at higher temperatures towards practical conditions has been a primary enduring goal. The recent report of room-temperature superconductivity at near-ambient pressure in nitrogen-doped lutetium hydride (Lu-H-N) by Dasenbrock-Gammon et al. (Hereafter referred as D-G) seems a great step approaching the ultimate goal. Specifically, they claimed evidence of superconductivity on Lu-H-N with a maximum Tc of 294 K at 1 GPa. However, the failure to observe the drastic temperature-dependent resistance change above 200 K in high-pressure synthesized Lu-H-N compounds, a prerequisite for superconductivity, by researchers worldwide in all independent follow-up studies casts a heavy shadow on the authenticity of the claims. The sober questions are: what is the sample that produces the sharp resistance jump near room temperature? What are the reasons for the non-reproducibility of others who follow the D-G method of synthesis and the inscrutable low success rate (35%) in synthesizing the right sample even for the authors in Ref. 1? What causes the observed sharp resistance jump? Here, with a well-controlled experiment protocol, we repeatedly reproduced the near room-temperature sudden change of electrical resistance in the Lu-H-N sample, and we could quantitatively compare its behavior with the initial pure Lu in a normal metallic state. These results enable us to scrutinize the origin for the near-room temperature sharp resistance change, which is attributed to a metal-to-poor-conductor transition rather than superconductivity.

Percolation-induced resistivity drop in cold-pressed LuH2

The near room-temperature upsurge of electrical resistivity in Lu-H-N is not superconductivity, but a metal-to-poor-conductor transition

Unveiling a Novel Metal-to-Metal Transition in LuH2: Critically Challenging Superconductivity Claims in Lutetium Hydrides

Origin of the near-room temperature resistance transition in lutetium with H2/N2 gas mixture under high pressure

Electronic and magnetic properties of Lu and LuH$_2$

Current percolation model for the special resistivity behavior observed in Cu-doped Apatite

Robust magnetism against pressure in non-superconducting samples prepared from lutetium foil and H2/N2 gas mixture

Absence of near-ambient superconductivity in LuH$_{2\pm\text{x}}$N$_y$

Absence of Superconductivity in LiPdHx

High-temperature Superconductivity of Pm 3 N Lu 4 H 23 Immersed in an As-Synthesized Lutetium Polyhydride

Investigations of pressurized Lu-N-H materials by using the hybrid functional

Thermodynamic properties and enhancement of diamagnetism in nitrogen doped lutetium hydride synthesized at high pressure

Influence of Temperature, Pressure, and Oxygen Fugacity on the Electrical Conductivity of Dry Eclogite, and Geophysical Implications

Leading components and pressure-induced color changes in N-doped lutetium hydride

Superconductivity at ambient pressure in hole-doped LuH$_3$

Pressure induced color change and evolution of metallic behavior in nitrogen-doped lutetium hydride

Effect of water on the electrical conductivity of lower crustal clinopyroxene

Absence of near-ambient superconductivity in LuH2±xNy

Absence of Near-Ambient Superconductivity in LuH 2± X N Y

Pressure effect on the topologically nontrivial electronic state and transport of lutecium monobismuthide

Stabilization of High‐Pressure Phase of Face‐Centered Cubic Lutetium Trihydride at Ambient Conditions