Absence of near-ambient superconductivity in LuH$_{2\pm\text{x}}$N$_y$

Xue Ming,Ying-Jie Zhang,Xiyu Zhu,Qing Li,Chengping He,Yuecong Liu,Bo Zheng,Huan Yang,Hai-Hu Wen

DOI: https://doi.org/10.1038/s41586-023-06162-w

2023-06-02

Abstract:Recently near-ambient superconductivity was claimed in N-doped lutetium hydride (ref. 1). This induces a worldwide fanaticism about the dream of room temperature superconductivity under low pressures. By using a high pressure and high temperature synthesis technique, we have successfully obtained the nitrogen doped lutetium hydride (LuH$_{2\pm\text{x}}$N$_y$) with a dark-bluish color and a structure with the space group of $Fm\bar{3}m$ evidenced by x-ray diffraction. This structure is the same as that reported in ref. 1. The energy dispersive X-ray spectroscopy (EDS) confirmed the existence of nitrogen in some areas of the samples. At ambient pressure, we witness a kink of resistivity and magnetization at about 300 K, which may correspond to a rearrangement of hydrogen/nitrogen atoms, namely a structural transition. However, by applying a pressure from 1 GPa to 6 GPa, we have seen a progressively optimized metallic behavior without showing superconductivity down to 10 K. Temperature dependence of magnetization shows a roughly flat feature between 100 and 320 K, and the magnetization increases with magnetic field at 100 K, all these are not expected for superconductivity at 100 K. Thus, we conclude the absence of near-ambient superconductivity in this nitrogen-doped lutetium hydride under pressures below 6 GPa.

Superconductivity

What problem does this paper attempt to address?

The paper primarily investigates whether nitrogen-doped lutetium hydride (LuH₂±xNy) exhibits superconductivity under near-ambient pressure conditions. Specifically, the research team attempts to verify a recent claim that nitrogen-doped lutetium hydride can exhibit superconductivity near room temperature (approximately 294 K) under a pressure of only 1 GPa.

To conduct this study, the authors first successfully synthesized dark blue nitrogen-doped lutetium hydride samples using high-temperature and high-pressure synthesis techniques. X-ray diffraction confirmed that the crystal structure of the samples was consistent with previous reports, with a space group of Fm3̅m. Additionally, energy-dispersive X-ray spectroscopy (EDS) confirmed the presence of nitrogen in the samples.

However, in further experiments, the research team did not observe superconductivity under near-ambient pressure conditions. Specifically:

1. **Resistivity Measurements**: Under different pressures (from 1 GPa to 6 GPa), the resistivity as a function of temperature showed metallic behavior, but no superconducting transition or zero-resistance state was observed when the temperature dropped to 10 K.
2. **Magnetization Measurements**: The magnetization as a function of temperature remained almost constant between 100 K and 320 K, and the magnetization increased with increasing magnetic field, none of which are characteristic of the expected superconducting behavior.

In summary, the research team concluded that in their synthesized nitrogen-doped lutetium hydride samples, no superconductivity was observed under near-ambient pressure conditions within the pressure range below 6 GPa. This conclusion contradicts previous reports suggesting that this material might exhibit near-room-temperature superconductivity at lower pressures.