New-type Hf-based NASICON electrolyte for solid-state Na-ion batteries with superior long-cycling stability and rate capability

Haoqing Tian,Shan Liu,Lijun Deng,Ling Wang,Lei Dai

DOI: https://doi.org/10.1016/j.ensm.2021.04.026

IF: 20.4

2021-08-01

Energy Storage Materials

Abstract:<p>The NASICON electrolyte with good chemical stability, suitable three-dimensional ion channel, high mechanical strength and wide electrochemical window, has been considered to be the one of most promising electrolytes for solid-state Na-ion batteries. However, the unsatisfactory ionic conductivity and large interface resistance severely limit its practical application. Herein, a new-type Hf-based NASICON electrolyte Na_3.2Hf_1.9Ca_0.1Si₂PO₁₂ is synthesized, the conductivity of which can reach 1.07 × 10⁻³ S cm⁻¹ at room temperature and the stability electrochemical window can reach 8.80 V. In addition, a mixed-ion-electron interphase was constructed on the surface of Na_3.2Hf_1.9Ca_0.1Si₂PO₁₂ which can guarantee a close contact and fast charge transfer between sodium and the electrolyte. The batteries with this new-type electrolyte can cycle stably more than 2400 hours at room temperature and the critical current density can reach 1.9 mA cm⁻². Even the current density reaches 2.0 mA cm⁻², there was still no obvious short circuit, which was the highest value in similar works. The full cell of Na/Na₃V₂(PO₄)₃ with this electrolyte can maintain a capacity of 103.1 mAh g⁻¹ at 0.5 C without capacity decaying even after more than 300 cycles.</p>

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology