The microstructures, magnetic properties and impedance analysis of Mn–Zn ferrites doped with B2O3

J Fan,F.R Sale

DOI: https://doi.org/10.1016/s0955-2219(00)00230-2

IF: 5.7

2000-01-01

Journal of the European Ceramic Society

Abstract:The relationship between the microstructure, magnetic properties and impedance spectroscopy of Mn–Zn ferrites doped with B2O3 (up to 0.5 wt.%) has been further investigated. The ferrites were prepared by using a citrate gel processing route. A uniform microstructure with relatively small grains (9.6±0.7 μm) is observed for undoped ferrites (boron-free), which enables good magnetic properties to be achieved (initial permeability μi is 2400, power loss PL is 26.3 kW/m3 at 100 mT).The results on the samples doped with B2O3 show that the doping does not benefit the magnetic properties of these gel-derived ferrites, but it promotes grain growth significantly. Discontinuous grain growth at low doping levels (<0.2 wt.%) results in poor magnetic properties. A maximum value of the initial permeability (μi: ∼2600) and a second minimum value (37.2 kW/m3 at 100 mT) in power loss are obtained at the 0.25 wt.% B2O3 doping level when the sample has a relatively uniform microstructure with larger grain size (39.5±3.3 μm). With further increases in B2O3 doping (⩾0.5 wt.%), the increased porosity and presence of a B-rich phase result in deteriorated magnetic properties. The results of impedance measurement are closely related to the changes in the microstructure which result from these B2O3 additions. By using two models for impedance measurement analysis (The Koops’ model and the simple model), the contributions of B2O3 to grain boundary resistivity and bulk resistivity can be separated. It is shown that, whilst B2O3 has previously been considered to act as only a grain boundary additive, the impedance analysis indicates that both boundary resistivity and grain (bulk) resistivity are increased, thus implying the possible solution of some B2O3 within the ferrite spinel structure or an effective change in composition of grain as result of presence of B2O3 at the grain boundaries.

materials science, ceramics