Abstract:The relationship between the microstructure, magnetic properties and impedance spectroscopy of Mn–Zn ferrites doped with B2O3 (up to 0.5 wt.%) has been further investigated. The ferrites were prepared by using a citrate gel processing route. A uniform microstructure with relatively small grains (9.6±0.7 μm) is observed for undoped ferrites (boron-free), which enables good magnetic properties to be achieved (initial permeability μi is 2400, power loss PL is 26.3 kW/m3 at 100 mT).The results on the samples doped with B2O3 show that the doping does not benefit the magnetic properties of these gel-derived ferrites, but it promotes grain growth significantly. Discontinuous grain growth at low doping levels (<0.2 wt.%) results in poor magnetic properties. A maximum value of the initial permeability (μi: ∼2600) and a second minimum value (37.2 kW/m3 at 100 mT) in power loss are obtained at the 0.25 wt.% B2O3 doping level when the sample has a relatively uniform microstructure with larger grain size (39.5±3.3 μm). With further increases in B2O3 doping (⩾0.5 wt.%), the increased porosity and presence of a B-rich phase result in deteriorated magnetic properties. The results of impedance measurement are closely related to the changes in the microstructure which result from these B2O3 additions. By using two models for impedance measurement analysis (The Koops’ model and the simple model), the contributions of B2O3 to grain boundary resistivity and bulk resistivity can be separated. It is shown that, whilst B2O3 has previously been considered to act as only a grain boundary additive, the impedance analysis indicates that both boundary resistivity and grain (bulk) resistivity are increased, thus implying the possible solution of some B2O3 within the ferrite spinel structure or an effective change in composition of grain as result of presence of B2O3 at the grain boundaries.

Microstructural And Electromagnetic Properties Of Mn-Zn Ferrites With Low Melting-Point Nonmagnetic Sb3+ Ions

Effect of Mn substitution on the magnetic properties of MgCuZn ferrites

Magnetic and Electrical Properties of Low-Temperature Sintered Mn-doped NiCuZn Ferrites

Microstructures and magnetic properties of NiCuZn ferrite ceramics doped with MnO2–Bi2O3

Influence of Sr2+ Doping Quantity on Microstructure and Magnetic Performance of Z Type Hexagonal Ferrite

Investigation on the Micro-Structure and Magnetic Properties of LMZBS-Bi2O3 Doped Low-Temperature Sintered NiCuZn Ferrites

Optimum Sintering Temperatures and Magnetic Properties of Mn-Zn Ferrites Doped with Y2O3

Effects of Fe2+ content in raw materials on Mn–Zn ferrite magnetic properties

Study on Electromagnetic Properties of MnZn Ferrites with Fe-poor Composition

Effect of Mn Doping on Physical Properties of Y-Type Hexagonal Ferrite

Effect of Zn Substitution on Morphology and Magnetic Properties of Cufe2o4 Nanofibers

Effects of Bi doping on the sintering and magnetic properties of Ni-Zn-Cu ferrites

The microstructures, magnetic properties and impedance analysis of Mn–Zn ferrites doped with B2O3

Preparation of low-temperature sintered Mn doped Mg-Cu-Zn ferrites by sol-gel self-combustion method

Mn Doping of BiFeO3 for Microstructure and Electromagnetic Characteristics

Effects of Fe, Mn Individual Doping and (Fe, Mn) Co-Doping on Ferromagnetic Properties of Co2Si Powders

Microstructure and Magnetic Properties in Mn-doped Nd–Fe–B Magnets

Improving soft magnetic properties of Mn-Zn ferrite by rare earth ions doping

Electromagnetic Properties Of Mn-Doped Nicuzn Ferrites Prepared By Sol-Gel Auto-Combustion

The Influence of Mn Dopant on the Electromagnetic Properties of Nicuzn Ferrite

Effect of Copper Substitution on the Dielectric and Magnetic Properties of Low-Temperature-Sintered Z-type Ferrites