Abstract:Abstract We report a comprehensive study of the growth dynamics in highly periodic, composition tunable InAsSb nanowire (NW) arrays using catalyst-free selective area molecular beam epitaxy. Employing periodically patterned SiO 2 -masks on Si (111) with various mask opening sizes (20–150 nm) and pitches (0.25–2 μ m), high NW yield of >90% (irrespective of the InAsSb alloy composition) is realized by the creation of an As-terminated 1 × 1-Si(111) surface prior to NW nucleation. While the NW aspect ratio decreases continually with increasing Sb content ( x Sb from 0% to 30%), we find a remarkable dependence of the aspect ratio on the mask opening size yielding up to ∼8-fold increase for openings decreasing from 150 to 20 nm. The effects of the interwire separation (pitch) on the NW aspect ratio are strongest for pure InAs NWs and gradually vanish for increasing Sb content, suggesting that growth of InAsSb NW arrays is governed by an In surface diffusion limited regime even for the smallest investigated pitches. Compositional analysis using high-resolution x-ray diffraction reveals a substantial impact of the pitch on the alloy composition in homogeneous InAsSb NW arrays, leading to much larger x Sb as the pitch increases due to decreasing competition for Sb adatoms. Scanning transmission electron microscopy and associated energy-dispersive x-ray spectroscopy performed on the cross-sections of individual NWs reveal an interesting growth-axis dependent core–shell like structure with a discontinuous few-nm thick Sb-deficient coaxial boundary layer and six Sb-deficient corner bands. Further analysis evidences the presence of a nanoscale facet at the truncation of the (111)B growth front and {1-10} sidewall surfaces that is found responsible for the formation of the characteristic core–shell structure.

Large-composition-range pure-phase homogeneous InAs$_{1-x}$Sb$_x$ nanowires

Silver-assisted growth of high-quality InAs 1- x Sb x nanowires by molecular-beam epitaxy

Realization Of Vertically Aligned, Ultrahigh Aspect Ratio Inassb Nanowires On Graphite

Controlled-Direction Growth of Planar InAsSb Nanowires on Si Substrates Without Foreign Catalysts

Sb-Induced Phase Control of Inassb Nanowires Grown by Molecular Beam Epitaxy

From Twinning to Pure Zincblende Catalyst-Free Inas(Sb) Nanowires

Controlled Synthesis of Phase-Pure InAs Nanowires on Si(111) by Diminishing the Diameter to 10 Nm.

Control of morphology and crystal purity of InP nanowires by variation of phosphine flux during selective area MOMBE

Stoichiometric effect on electrical and near-infrared photodetection properties of full-composition-range GaAs1−xSbx nanowires

Ultrasmall Single-Crystal Indium Antimonide Nanowires

Catalyst-Free Heteroepitaxial MOCVD Growth of InAs Nanowires on Si Substrates

Length and composition tunable Sb–Bi–S nanowires for optoelectronic devices prepared via an isostructure-favored solvothermal synthesis

Growth of InAs Quantum Dots on GaAs Nanowires by Metal Organic Chemical Vapor Deposition.

Selective area growth of in-plane InAs nanowires and nanowire networks on Si substrates by molecular-beam epitaxy

Antimony‐Rich GaAs x Sb 1− x Nanowires Passivated by Organic Sulfides for High‐Performance Transistors and Near‐Infrared Photodetectors

High-quality ultralong Bi2S3 nanowires: structure, growth, and properties

Growth dynamics and compositional structure in periodic InAsSb nanowire arrays on Si (111) grown by selective area molecular beam epitaxy

The Self-Catalyzed Growth of GaAsSb Nanowires on a Si (111) Substrate Using Molecular-Beam Epitaxy

Recent Progress on Infrared Photodetectors Based on InAs and InAsSb Nanowires

Free-Standing Two-Dimensional Single-Crystalline InSb Nanosheets.

Self-catalysed InAs 1-x Sb x nanowires grown directly on bare Si substrates