Abstract:To date, the most commonly used aluminum alloys for additive manufacturing are eutectic/near-eutectic alloys. However, fabricating high strength aluminum parts has not yet been fully investigated due to solidification cracking and porosity formation, which make these alloys very hard to be processed. Electron beam selective melting (EBSM) of aluminum alloys has some advantages over selective laser melting. The process is not affected by reflectivity of aluminum powders, and parts exhibit less induced thermal stresses. In addition, oxidation is reduced due to vacuum condition. Therefore, the process provides high potential for the fabrication of aluminum alloys, specifically, Al2024 alloy which is widely used in different industries such as automotive and airline industries. Hence, these industries are highly benefitted from being able to build defect-free AM parts. This study is significant because Al2024 alloy is highly susceptible to solidification cracking and porosity formation, and crack-free samples with high relative densities have not been built by EBM process previously. The baseplate preheating temperature was set to 350 degrees C, and samples were fabricated by applying a proper powder bed preheating configuration for each layer. Different sets of processing parameters were used to investigate their effect on the performance of the parts. Archimedes technique was used to measure the relative density of samples, ranging from 95% to full-dense. The results showed that higher relative densities could be achieved by increasing the input energy to an optimum value; however, by further increasing the energy, the relative density decreases, which can be attributed to porosity formation. SEM and EBSD results showed equiaxed grains in a crack-free microstructure. Grain structure consisted of high angle grain boundaries having different crystallographic orientations with a few subgrains. Additionally, AlCuMnFe, AlCuMnFeSi, and eutectic Al2Cu phases were uniformly distributed in the alpha phase matrix. Microhardness results showed an almost uniform change of hardness values in both horizontal and vertical sections, ranging from 100 HV to 110 HV for as-built samples. Moreover, tensile and yield strengths of as-built samples reached 314 MPa and 191 MPa, respectively, which can be further increased by a proper post-processing treatment. (C) 2020 Elsevier B.V. All rights reserved.

X-ray and optical crystallographic parameters investigations of high frequency induction melted Al-(alpha-Al(2)O(3)) alloys

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Structure and mechanical behavior of ultrafine-grained aluminum-iron alloy stabilized by nanoscaled intermetallic particles

Improving strain hardening behavior in nano-intermetallic reinforced aluminum in-situ composites through an optimized twostep thermal processing method; sintering and uniaxial forging

Homogenization heat treatment influence on microstructure evolution and mechanical properties of as-cast Al-Li-Cu-Mg-Zr alloy for lightweight aerospace application

Microstructures and Mechanical Properties of Ultralight Cast Al-3Li-XMg-0.1Zr Alloys

Microstructure and Mechanical Properties of In-Situ Α-Al2o3p/al-12si Composites Fabricated by Direct Melt Reaction Method with Aid of Electromagnetic Stirring

Sustainability through Optimal Compositional and Thermomechanical Design for the Al-7XXX Alloys: An ANOVA Case Study

Selective electron beam melting of high strength Al2024 alloy; microstructural characterization and mechanical properties

Influence of the Al Content on the Properties of Mechanically Alloyed CoCrFeNiMnXAl20-X High-Entropy Alloys

Atom Location by Channeling-Enhanced Microanalysis (ALCHEMI) Study of Structure of Complex Concentrated Alloys Derived From FeAl Iron Aluminide

Influence of the iron additive on the microstructural behavior of an aluminum-copper foundry alloy B206

Microstructure and Mechanical Properties Determined in Compressive Tests of Quasi-Rapidly Solidified NiAl-Cr(Mo)-Hf Eutectic Alloy after Hot Isostatic Pressure and High Temperature Treatments

Microstructure, hardening and mechanical properties of hypoeutectic Al‐Ce‐Ni alloys with Zr and Zr+Sc additions and the effect of ultrasonic melt processing

Microstructural Evolution of a High-Strength Zr-Ti-Modified 2139 Aluminum Alloy for Laser Powder Bed Fusion

Effect of CuO Nanostructure Addition and Cooling Rate on the Microstructure and Mechanical Characteristics of Hypoeutectic Al-2wt.%Si Alloy

Microstructural Characterization and Mechanical Properties of AlMg Alloy Fabricated by Additive Friction Stir Deposition

Production and Characterization of Fine-Grained Multielement AlCoxCrFeNi (x = 1, 0.75, 0.5) Alloys for High-Temperature Applications

Thermal Analysis of ALSI10MG Alloy and Heat Treatment Hardening

Design, microstructure and thermal stability of a novel heat-resistant Al-Fe-Ni alloy manufactured by selective laser melting