Stabilization of Li 2 MnO 3 phase by Mg doping suppressing irreversible oxygen loss and Mn ions migration

Zhiyuan Ma,Zihao Zheng,Xuelin Tao,Teng Hui,Hanqi Yu,Fengli Bei

DOI: https://doi.org/10.1016/j.jallcom.2023.173367

IF: 6.2

2024-01-11

Journal of Alloys and Compounds

Abstract:Li-rich Mn-based oxide cathode material has attracted people's attention in that their higher specific capacity, which is attributed to their unique biphasic structure. When the voltage is greater than 4.5 V, the Li 2 MnO 3 phase is activated to provide a high specific capacity. But during the cycling process, the Li 2 MnO 3 phase is continuously activated. During this process, O 2 will be released and transition metal (TM) ions will migrate, leading to structural phase transition, resulting in voltage decay and capacity loss. In this work, 2 wt% Mg-doped Li 1.18 Mg 0.02 Mn 0.54 Co 0.13 Ni 0.13 O 2 exhibits excellent electrochemical performance. After 100 cycles at 1 C, the capacity retention rate is 87.83% By introducing Mg at the position of Li in the TM layer, a more stable Mg-O bond is introduced, in which the inert Mg is not involved in the redox reaction but is fixed in the TM layer. The Li 2 MnO 3 phase is optimized by stabilizing the lattice oxygen to make the Li 2 MnO 3 phase more stable, so as to suppress the irreversible oxygen loss and slow down the structural phase transition. Improved the issue of low initial Coulomb efficiency of materials, the voltage attenuation is alleviated, and the cycle stability is improved.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering