Abstract:Bearing steel (GCr15) is widely used in key parts of mechanical transmission for its excellent mechanical properties. Electrochemical machining (ECM) is a potential method for machining GCr15, as the machining process is the electrochemical dissolution of GCr15 regardless of its high hardness (>50 HRC). In ECM, NaNO3 solution is a popular electrolyte, as it has the ability to help in the nonlinear dissolution of many metallic alloy materials, making it useful for precision machining. However, due to high carbon content of GCr15, the electrochemical dissolution of GCr15 is unique, and there is always a black layer with high roughness on the machined surface, reducing the surface quality. In order to improve the electrochemical machining of GCr15 with a high surface quality, the surface characteristics of GCr15 in ECM were investigated. The anodic polarisation curve in the NaNO3 electrolyte was measured and electrochemical dissolution experiments were conducted with different current densities. SEM, XRD, and XPS were employed to analyse the surface morphology and composition formed on the machined surface at different current densities. The initial results showed that there were two parts (black part and bright part) formed on the machined surface when a short circuit occurred, and the test results suggested that the black part contained a mass of Fe3O4 while the bright part was composed of mainly Fe and Fe3C. Further investigation uncovered that a black flocculent layer (Fe3O4) always formed in a low current density (32 A/cm2) with high roughness. With the current density increased, the amount of black flocculent layer was reduced, and Fe3C particles appeared on the machined surface. When the current density reached 81 A/cm2, the entire flocculent oxide layer was removed, only some spherical Fe3C particles were inserted on the machined surface, and the roughness was reduced from Ra7.743 μm to Ra1.783 μm. In addition, due to exposed Fe3C particles on the machined surface, the corrosion resistance of the machined surface was significantly improved. Finally, circular arc grooves of high quality were well manufactured with current density of 81 A/cm2 in NaNO3 electrolyte.

Experimental examination on electrochemical machining of Mg/FeCoCrNiMn composite

Enhancing WEDM performance on Mg/FeCoCrNiMn HEA composites through ANN and entropy integrated COCOSO optimization

Investigation of Enhancing EDM Machining Performance of INCONEL Alloy Using Composite Electrodes

Experimental Investigation of MRR on Inconel 600 using Ultrasonic Assisted Pulse Electrochemical Machining

Parametric effect on material removal rate and surface roughness of electrical discharge machined magnesium alloy

Flat-end mill machining analysis of processed CrMnFeCoNi high-entropy alloys

Multi-Response Optimization of Electrochemical Machining Parameters for Inconel 718 via RSM and MOGA-ANN

Experimental Investigation and Optimization of Wire Electrical Discharge Machining for Surface Characteristics and Corrosion Rate of Biodegradable Mg Alloy

Experimental Investigations On The Electrochemical Machining Of D3 Die Steel Material And Multi-Objective Parameter Optimization

Investigation of Machining Rate and Surface Roughness in Wire EDM of Al6063/WC/ZrO2 Composite using Response Surface Methodology

Experimental Investigation of WE43(T6) magnesium metal matrix composites to enhance mechanical properties and EDM process parameters

Impact of Different Electrolytes on the Machining Rate in ECM Process

Effect of Mg on the Microstructure, Mechanical Properties, and Surface Roughness of Functionally Graded A413 Composite: Machine Learning Approach at Wire‐Cut Electric Discharge Machining Zone

Performance Analysis and Optimization of Different Electrode Materials and Dielectric Fluids on Machining of High Carbon High Chromium Steel in Electrical Discharge Machining

Experimental Investigation and Parametric Optimization during Magnetic Field-Assisted Electric Discharge Machining of Nimonic 90

Study of machining performance for electrochemical grinding of difficult-to-cut alloy U71Mn

Experimental investigation to assess the surface integrity in WEDM of Al-based hybrid composite material

Investigation of the effect of electrophoresis-assisted milling on machinability

Investigation of the Surface Characteristics of GCr15 in Electrochemical Machining

Experimental Investigations and Optimum Performance Evaluation of Wire-EDM Characteristics of Aluminium 6061-Magnesite Composites

Anode characteristics and electrochemical machining of U71Mn alloy in different electrolyte solutions