Investigation of Enhancing EDM Machining Performance of INCONEL Alloy Using Composite Electrodes

KT Shabarinathan,K Senthilkumar,N Kathiravan,RM Udhayachandran,Shabarinathan KT,K Senthil Kumar,Kathiravan N,Udhayachandran RM

DOI: https://doi.org/10.1088/2053-1591/ad1b09

IF: 2.025

2024-01-06

Materials Research Express

Abstract:In this research, an attempt was made to reinforce aluminium with graphite particles and use it as a tool material with the objective of combining the properties of aluminium and graphite. The micrograph confirms that the graphite particles were uniformly distributed over the aluminium matrix, density reduces and thermal conductivity increases with the addition of graphite particles. Material Removal Rate (MRR) peaks at 12A current before declining due to plasma channel expansion, an optimal Ton of 8μs ws observed, with 4μs Toff yielding higher MRR. Copper electrodes excel due to thermal conductivity, while 5% graphite in aluminum boosts MRR to 31.89mm3/min, additional graphite decreases MRR. TWR rises with shorter Toff until 6μs, then decreases. Gap control impacts TWR, with lower spark gaps causing higher TWR due to intense material removal, and higher gaps leading to increased TWR due to incomplete flushing. Copper electrodes have the lowest TWR due to their high melting temperature. The addition of graphite in aluminum reduces TWR at low currents but is less effective at higher currents. Surface roughness (Ra) decreases with higher current, reaching a minimum of 7.02μm at 12A. Optimal Ton is 8μs (7.56μm), while shorter Toff at 4μs and a 3mm gap yield the best Ra of 7.36μm with A4 composite tool. Copper electrodes result in higher Ra at higher currents, while graphite in aluminum improves surface quality, especially at 5% content. Arcing, an undesirable electrical discharge phenomenon in EDM, adversely affects machining. Experiments revealed a strong correlation between high duty cycles, duty ratios, and arcing propensity, with composite tools being more susceptible due to their variable conductivity. In contrast, non-composite tools, exemplified by copper, withstand higher duty ratios without arcing.

materials science, multidisciplinary

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to use aluminum - based composites as electrode materials in Electrical Discharge Machining (EDM) to improve the machining performance of INCONEL alloys. Specifically, the research aims to explore the effects of these composite electrodes on the Material Removal Rate (MRR), Tool Wear Rate (TWR) and Surface Roughness (Ra) by adding graphite particles in different proportions to the aluminum matrix. In addition, the research also investigates the arc phenomena of these composite electrodes during the machining process and their impact on the machining performance.

### Research Background
Electrical Discharge Machining (EDM) is an unconventional machining method that removes workpiece materials through electric spark discharges. EDM is widely used in industries such as aerospace, medical and precision engineering due to its advantages of low tool wear and the ability to machine complex shapes and hardened materials. However, choosing the appropriate electrode material is crucial for improving the efficiency and precision of EDM. Materials such as copper, graphite, copper - tungsten, brass and aluminum have been widely studied for EDM electrodes, but there are relatively few studies on aluminum - based composites as EDM electrodes.

### Research Objectives
1. **Improve Machining Performance**: By adding graphite particles in different proportions to the aluminum matrix, study the performance of these composite electrodes in EDM machining, especially their effects on MRR, TWR and Ra.
2. **Optimize Process Parameters**: Through experimental design and optimization techniques (such as the VIKOR method), determine the best combination of process parameters to achieve the optimal machining effect.
3. **Analyze Arc Phenomena**: Study the arc tendencies of different electrode materials at high duty cycles and the impact of arcs on machining performance.

### Main Findings
- **Material Removal Rate (MRR)**: The current reaches its peak at 12 A and then decreases due to the expansion of the plasma channel. The optimal Ton is 8 μs, and the MRR is the highest when Toff is 4 μs. The aluminum - based composite electrode with 5% graphite content performs best in terms of MRR, reaching 31.89 mm³/min.
- **Tool Wear Rate (TWR)**: As Toff increases, the TWR first rises and then falls. Due to its high melting point, the copper electrode has the lowest TWR. The aluminum - based composite electrode with 5% graphite content has a lower TWR at low currents, but the effect is not obvious at high currents.
- **Surface Roughness (Ra)**: As the current increases, Ra gradually decreases and reaches a minimum of 7.02 μm at 12 A. When the optimal Ton is 8 μs, Toff is 4 μs and the gap is 3 mm, the surface quality is the best.
- **Arc Phenomena**: High duty cycles have a strong correlation with arc tendencies. Composite electrodes are more prone to arc phenomena due to changes in their conductivity.

### Conclusion
This research has successfully developed a new type of EDM electrode material by adding graphite particles in different proportions to the aluminum matrix. This composite electrode performs excellently in improving the machining performance of INCONEL alloys, especially in terms of MRR and surface quality. However, the arc phenomenon is a problem that requires further research and control to ensure the stability and reliability of the machining process.