Hyperfine Interactions in Dichalcogenides CrxNbSe2 (x = 0.33, 0.5): A 93Nb NMR Study

A. G. Smolnikov,Yu. V. Piskunov,V. V. Ogloblichev,A. F. Sadykov,M. E. Kashnikova,N. A. Utkin,A. P. Gerashchenko,D. F. Akramov,N. V. Selezneva,N. V. Baranov

DOI: https://doi.org/10.1134/s0031918x23602524

2024-04-22

The Physics of Metals and Metallography

Abstract:For the first time, an 93 Nb NMR study of dichalcogenides Cr x NbSe 2 ( x = 0.33, 0.5) in the paramagnetic state was performed. Analysis of the 93 Nb NMR spectra revealed the presence in Cr x NbSe 2 of three magnetically nonequivalent niobium positions, whose immediate environment contains 0, 1, and 2 chromium ions, respectively. For each Nb position with a different number of chromium atoms in the immediate environment in Cr x NbSe 2 ( x = 0.33, 0.5), the values of the components of the magnetic shift and electric field gradient tensors at the position of the niobium nuclei were determined. Evidence was obtained of the formation in Cr 0.33 NbSe 2 of the ordering of chromium ion positions in the ab plane into a a 0 × a 0 superstructure. On the other hand, in Cr 0.5 NbSe 2 , no obvious indications of the formation of any superstructure of chromium ion positions were found. It has been established that the overlap of the 4 d and 5 s shells of niobium ions and the 3 d orbitals of chromium leads to the appearance of a positive hyperfine field induced by the magnetic moments of chromium on Nb nuclei. From the temperature dependences of the shift and susceptibility in Cr 0.5 NbSe 2 , an estimate of these induced hyperfine fields is made.

metallurgy & metallurgical engineering