The Magnetic Properties of NdMnxCr2−xSi2C (0 <x< 2)
Guofu Chen,Qianheng Du,Wenyun Yang,Youfang Lai,Jinbo Yang,Changsheng Wang,Jingzhi Han,Shunquan Liu,Yan Zhang,Honglin Du,Changsheng Zhang,Yuanhua Xia,Dong Zhou,Yingchang Yang
DOI: https://doi.org/10.1088/0022-3727/49/2/025001
2015-01-01
Abstract:Carbon was successfully introduced into NdMnxCr2-xSi2 serial compounds as an interstitial atom. The compounds with x <= 0.5 keep a CeMg2Si2-type structure while the structure changes slowly with increasing manganese content. Finally, a new superstructure was found and determined for x around 1.7. All the compounds for x = 1.1, 1.3, 1.5 and 1.7 have two magnetic phase transition temperatures around 43 and 314 K. What is more, a giant magnetocaloric effect has been observed around the lower phase transition temperature, T-R similar to 51 K, in NdMn1.7Cr0.3Si2C. The maximum values of the magnetic entropy change - Delta S-M for the field change of 2 T and 5 T are 14.9 J kg(-1) K-1 and 26.0 J kg(-1) K-1, which means the interstitial atom effect enhanced the MCE values for 85% and 63% compared to NdMn1.7Cr0.3Si2, respectively. NdMn1.7Cr0.3Si2C with first order magnetic transition but low hysteresis losses (thermal < similar to 0.58 K; magnetic field < similar to 0.12 T) can be a candidate for magnetic refrigerator applications in the temperature region near 50 K. Besides, two field-induced magnetic phase transitions were found in NdMn1.7Cr0.3Si2C among the temperature range from 53 to 60 K, and a linear relation between the phase transition field and temperature was found and analyzed.