Muti-Filler Composites Reinforced with Multiwalled Carbon Nanotubes and Chopped Carbon Fibers for the Bipolar Plate of Fuel Cells

Huili Wei,Guofeng Chang,Sichuan Xu,Jinling Liu
DOI: https://doi.org/10.3390/en17071603
IF: 3.2
2024-03-28
Energies
Abstract:To improve the conductivity and flexural strength of bipolar plates for proton-exchange membrane fuel cells, multi-filler-reinforced composites were prepared using graphite, multiwalled carbon nanotubes (MWCNTs), chopped carbon fibers (CCFs), and phenolic resin (PF). The effects of CCF content (0–6 wt.%) and MWCNT content (0–8 wt.%) on the flexural strength, electrical conductivity, interfacial contact resistance (ICR), density, hydrophobicity, and corrosion behavior of the composites were investigated. Results showed that the addition of a small number of CCFs (≤4 wt.%) effectively improved the flexural strength but slightly reduced the electrical conductivity and increased the ICR of the graphite/PF/CCF composites. Further addition of MWCNTs (≤6 wt.%) significantly improved the electrical conductivity and ICR of the graphite/PF/CCF/MWCNT composites, while maintaining high flexural strength. When the composites were filled with 4 wt.% CCFs and 2 wt.% MWCNTs, their electrical conductivity, flexural strength, ICR under 1.38 MPa, and contact angle were 272.8 S/cm, 43.1 MPa, 1.19 mΩ·cm2, and 101.5°, respectively. Compared to unreinforced composites, the electrical conductivity was reduced by 27.2%, the flexural strength was increased by 65.1%, and the composite possessed favorable hydrophobicity as well as corrosion behavior. This work reveals that CCFs and MWCNTs can effectively cooperate to improve composites' electrical and flexural strength properties.
energy & fuels
What problem does this paper attempt to address?
### What problems does this paper attempt to solve? This paper aims to solve the contradiction between the conductivity and the flexural strength of the bipolar plates in proton - exchange membrane fuel cells (PEMFCs) to improve their performance. Specifically: 1. **Background problems**: - Although pure graphite bipolar plates have excellent conductivity and corrosion resistance, they require high - temperature treatment (over 2,500°C), resulting in high costs. - Metal bipolar plates are prone to corrosion in an acidic environment, which affects the performance of fuel cells. - Graphite/polymer composite bipolar plates have good corrosion resistance and processing properties, but due to the brittleness of graphite, their mechanical properties are not ideal. 2. **Research objectives**: - By introducing multi - walled carbon nanotubes (MWCNTs) and chopped carbon fibers (CCFs) as reinforcing materials, prepare multi - filler composites to simultaneously improve the conductivity and flexural strength of the bipolar plates. - Explore the effects of different contents of CCFs (0 - 6 wt.%) and MWCNTs (0 - 8 wt.%) on the flexural strength, electrical conductivity, interfacial contact resistance (ICR), density, hydrophobicity and corrosion - resistant behavior of the composites. 3. **Specific problems**: - How to optimize the electrical conductivity and flexural strength of the composites by adding an appropriate amount of CCFs and MWCNTs without affecting or minimizing other properties as much as possible. - Study the effects of different filler ratios on various properties of the composites, and find the optimal ratio so that the composites meet the requirements of PEMFCs bipolar plates. ### Conclusion It was found through experiments that when the CCFs content in the composite is 4 wt.% and the MWCNTs content is 2 wt.%, the electrical conductivity of the composite is 272.8 S/cm, the flexural strength is 43.1 MPa, the interfacial contact resistance is 1.19 mΩ·cm², and the contact angle is 101.5°. Compared with the unreinforced composite, the electrical conductivity decreased by 27.2%, but the flexural strength increased by 65.1%, and it has good hydrophobicity and corrosion - resistant properties. This indicates that CCFs and MWCNTs can effectively work in synergy to improve the electrical and mechanical properties of the composites.