Abstract:In this work, we report the evolution behavior of Fe and Fe-rich phases in the high-Fe concentration recycled Al-Si-Mg aluminum melt with and without alloying elements (Mn, Cr, Co) introduced. Firstly, the thermodynamic calculations reveal that the addition of Mn, Cr, and Co could improve the nucleation temperature of the Fe-rich phase. Moreover, four solidified ingots for Al-10Si-0.5Mg-1Fe alloy(base alloy) and the base alloy with 1.3 wt% Mn, 0.8 wt% Cr, and 0.8 wt% Co added, respectively, were prepared by holding the melt for 30 min at 610 °C after all the raw materials were fully melted. Microstructure examination revealed that the addition of Co resulted in the formation of the needle-like Fe-rich phase, which further leads to a poor settling effect and low iron removal efficiency. In contrast, the addition of Mn and Cr favors converting β-AlFeSi into α-AlFeMnSi, and forming the Chinese script and fish-bone Fe-rich phase. The size of the Fe-rich phase formed after adding Cr is smaller, while the residual Fe content after adding Mn is less. Also, the sludge phase at the bottom of the ingot presents a polygonal shape and long rod shape after adding Mn and Cr, respectively. Further, the Mn alloying increases the particle size of the sludge, while Cr refines the sludge phase and increases the aspect ratio (length/width ratio) of the sludge. Particularly, for Al-Si-Mg alloy with 1.0% Fe content, the superior mechanical properties are obtained by adding 0.8 wt% Cr, and the tensile strength reaches 136 MPa. After adding 1.3 wt% Mn, the Fe content of the upper section is reduced to 0.37 wt%, and the Fe removal rate achieves 63%. The obtained results provide some guidelines for achieving high iron separation efficiency in recycled aluminum-silicon alloy melts.

Mechanism of Fe removal by Sn addition in Al-7Si-1Fe alloy

Maintaining High Saturation Magnetic Flux Density and Reducing Coercivity of Fe-based Amorphous Alloys by Addition of Sn

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Regulating the Microstructure and Mechanical Properties in Cast Al–3Li–2Cu-0.15Zr Alloy Via Sn Addition and Heat Treatment

Sn-Sc microalloying-induced property improvement and micromechanisms of an Al-Mg-Si alloy

Evolution behavior of Fe and Fe-rich phases in high-Fe concentration Al-Si-Mg alloy with Mn, Cr, and Co alloyed

Influences of Sn on Fe phase segregation and properties of Cu-5Fe alloy

STUDY ON FE REMOVAL PROCESS IN AL-SI SERIES OF ALLOYS

Purification of metallurgical-grade silicon using Si–Sn alloy in presence of Hf, Zr, or Ti

Uncovering the effects of neutralizing elements (Co, Mn and Cr) on the Fe-rich intermetallic formation in Al–Si–Cu alloys

Study of the evolution mechanisms of Fe-rich phases in Al-Si-Fe alloys with Mn modification using synchrotron X-ray imaging

Improving the Mechanical Properties and Intergranular Corrosion Resistance of Al-9.2Mg-0.8Mn-0.2Zr Alloy by Sn Addition

Effect of Initial Fe Content on Microstructure and Mechanical Properties of Recycled Al-7.0Si-Fe-Mn Alloys with Constant Mn/Fe Ratio

Effect of Si on Fe-rich intermetallic formation and mechanical properties of heattreated Al-Cu-Mn-Fe alloys

Revealing the nucleation and growth mechanisms of Fe-rich phases in Al–Cu–Fe(-Si) alloys under the influence of Al–Ti–B

Impurity phases and their removal in Si purification with Al–Si alloy using transition metals as additives

Microstructure, Mechanical Properties and First Principle Calculation of Mg-7Al (-2Sn) Alloys Prepared by Vacuum Die-casting

Mechanism of Iron-rich Compound Modification and Purification in Recycled AlSi10MgFe Alloy with Manganese

Effect of Sn element on the interfacial reinforced AlN/Cu joint brazed by Ag–Cu–Ti–(Snx) filler

Effect of Sn contents on natural aging and precipitation hardening in Al-Mg-Si alloys

The role of Sn element on the deformation mechanism and precipitation behavior of the Al–Cu–Mg alloy