Abstract:A high Fe content easily produces Fe-rich phases with a harmful morphology, resulting in a huge detrimental effect on the properties and recycling ability of Al-Si alloys. Therefore, finding ways to effectively transform Fe-rich phases to form a beneficial phase or shape is of great significance. Accordingly, Al-Si-based alloys with Fe contents ranging from 0.1 wt.% to 2.0 wt.% were modified by different Mn additions. Moreover, experiments combined with simulations were utilized to comprehensively analyze the mechanism of Mn on the morphology and microstructural evolution of Fe-rich phases from different perspectives. The current findings determine that adding different Fe contents changes the phase-transition reactions in alloys. Without Mn, and by increasing the Fe content from 0.1 wt.% to 2.0 wt.%, the Fe-rich phases gradually convert from a skeleton-shaped α-Al8Fe2Si (<0.25 wt.%) to β-Al9Fe2Si2 with a fibrous (0.5 wt.%), needle-like (1.0 wt.%) and plate-like shape without curvatures (2.0 wt.%). The maximum length and mean aspect ratio increase from 12.01 μm to 655.66 μm and from 1.96 to 84.05, while the mean curvature decreases from 8.66 × 10−2 μm−1 to 8.25 × 10−4 μm−1. The addition of 0.35 wt.% Mn promotes a new Chinese-character and petal-shaped α-Al15(FeMn)3Si2, with an atomic ratio of Fe and Mn of 1:1 when the Fe content is lower than 0.5 wt.%, while it transforms to β-Al15(FeMn)3Si2 with an atomic ratio of 5:1, presenting as a refined plate-like shape with a certain curvature, as the Fe content increases to 2.0 wt.%. Mn alters the phase reactions and increases the threshold of the Fe content required for β-Al15(FeMn)3Si2, limiting the formation and growth of them simultaneously in time and space. The enrichment of Mn atoms and solute diffusion at the growth front of β-Al15(FeMn)3Si2, as well as the strong atomic-binding ability, can deflect the growth direction of β-Al15(FeMn)3Si2 for it to have a certain curvature. Additionally, the enriched Mn atoms easily form α-Al15(FeMn)3Si2 and cause the long β-Al15(FeMn)3Si2 to be broken and refined to further reduce the damages caused to the alloy's performance. Ultimately, the maximum length and mean aspect ratio can be effectively reduced to 46.2% and 42.0%, respectively, while the mean curvature can be noticeably increased by 3.27 times with the addition of Mn.

Mechanism of Iron-rich Compound Modification and Purification in Recycled AlSi10MgFe Alloy with Manganese

Effect of Mn/Fe Ratio on Fe Removal Efficiency and Tensile Ductility of an Al–7.0Si–2.4Fe Alloy

Effect of Initial Fe Content on Microstructure and Mechanical Properties of Recycled Al-7.0Si-Fe-Mn Alloys with Constant Mn/Fe Ratio

Evolution behavior of Fe and Fe-rich phases in high-Fe concentration Al-Si-Mg alloy with Mn, Cr, and Co alloyed

Formation and sedimentation of Fe-rich intermetallics in Al−Si−Cu−Fe alloy

Study of the evolution mechanisms of Fe-rich phases in Al-Si-Fe alloys with Mn modification using synchrotron X-ray imaging

Effects of Mn addittion, cooling rate and holding temperature on the modification and purification of iron-rich compounds in AlSi10MnMg(Fe) alloy

Synergistic effects of Mn and B on iron-rich intermetallic modification of recycled Al alloy

Microstructure and Mechanical Properties of Ductile Aluminium Alloy Manufactured by Recycled Materials

Developing Al–Fe–Si alloys with high thermal stability through tuning Fe, Si contents and cooling rates

Evolutionary mechanism of the precipitation behavior and organization of iron-containing intermetallic phase during solidification of recycled high-Fe Al-Zn-Mg-Cu melts

Optimizing the Morphology and Solidification Behavior of Fe-Rich Phases in Eutectic Al-Si-Based Alloys with Different Fe Contents by Adding Mn Elements

Modification of Iron-Rich Phase in Al-7Si-3Fe Alloy by Mechanical Vibration during Solidification

Iron Intermetallic Phases in the Alloy Based on Al-Si-Mg by Applying Manganese

Effects of Fe Content on the 3D Morphology of Fe-rich Phases and Mechanical Properties of Cast Al-Mg-Si Alloy

Revealing the influence of Fe on Fe-rich phases formation and mechanical properties of cast Al-Mg-Mn-Fe alloys

Fabrication of CrSi2-Containing Master Alloys for Modification of Fe-Containing Intermetallic Compounds in Aluminum Alloys

"EFFECTIVE REDUCTION OF IRON IMPURITIES IN RECYCLED ALUMINIUM-SILICON ALLOY TYPE LM-6 THROUGH SEDIMENTATION AND FILTRATION WITH SYNTHESIZED Mn, Cr and Zr TRANSITION METAL POWDERS"

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

A Formation Map of Iron-Containing Intermetallic Phases in Recycled Cast Aluminum Alloys

Melt Superheating on the Microstructure and Mechanical Properties of Diecast Al-Mg-Si-Mn Alloy