ZnI 2 post-processing of CsPbBr 3 quantum dots for red, stable, and low-threshold amplified spontaneous emission

Sijian Zhang,Jian Hu,Shuo Huang,Junxi Zhang,Mei Lyu,Hongbo Lu,Jun Zhu

DOI: https://doi.org/10.1063/5.0091905

IF: 4

2022-05-30

Applied Physics Letters

Abstract:All inorganic cesium lead halide perovskite (CsPbX 3 ; X = Cl, Br, or I) quantum dots (QDs) have received widespread attention as a class of favorable optical gain materials. The key issue of CsPbX 3 perovskites is their instability under light or exposure to air. Notably, the inherent phase instability of CsPbI 3 QDs severely restricts the development of red-light emission. Herein, we propose a simple method to post-process CsPbBr 3 QDs with a ZnI 2 solution. The prepared CsPbBr y I 3−y (named CPBI- z, where z corresponds to the photoluminescence peaks' position) QDs exhibit adjustable photoluminescence in the range of 550–640 nm. The photoluminescence quantum yield is increased from 73.3% to 97.2% as the surface defects of QDs are passivated by I − and Zn 2+ . Compared with the pristine CsPbBr 3 QDs, the post-processed QDs are more stable under ultraviolet irradiation and in the air. Aside from that, under 532 nm nanosecond laser excitation, CPBI- z QD films exhibit excellent amplified spontaneous emission performance. The CPBI-640 QD film shows a low threshold, 102 μJ cm −2 for red stable amplified spontaneous emission.

physics, applied