Abstract:The study demonstrates that applying an electric current during solidification significantly refines the primary Si phase. Moreover, adding phosphorus enhances this effect, particularly at 10 ppm, which is below the critical threshold of 20 ppm. The combined approach leads to improved nucleation and dispersion of aluminum phosphide, optimizing the microstructure for enhanced alloy performance. The efficient processing of hypereutectic Al–Si alloys depends on controlling the microstructure of the primary Si phase during solidification. This study investigates the effects of electric current and phosphorus (P) addition on the refinement of primary Si, with the results confirming that applying electric current during solidification refines the primary Si phase; introducing P further enhances this refinement. Notably, when 10 ppm of P is added (below the identified critical amount of 20 ppm), an improved refinement effect is observed compared with the application of either electric current or P alone. Applying an electric current generates a circulating flow within the melt, resulting in an increased cooling rate, which leads to improved nucleation behavior for the primary Si phase. In addition, the circulating flow generated within the melt influences the dispersion of aluminum phosphide during nucleation. Adding P at concentrations above 40 ppm does not yield further benefits, suggesting a saturation point for its efficacy. This study demonstrates that the concurrent electric current application and minimal P addition can significantly enhance the refinement of primary Si phases, offering a potent approach for optimizing the microstructural properties of hypereutectic Al–Si alloys.

Possibility of Complete Collecting Eutectic Si and Primary Si as Purified Si During Al-Si Solvent Refining with Zr Additions

Mechanism of boron removal of primary Si phases and morphology evolution of impurity phases during slow cooling solidification refining of Al-30wt.%Si alloy with Zr additions

A High-Efficiency and Energy-Saving Method for Purifying Industrial Silicon for Silicone Use

Mechanism of ZrB2 Formation in Al–Si Alloy and Application in Si Purification

Impurity phases and their removal in Si purification with Al–Si alloy using transition metals as additives

Efficient separation of bulk Si and enhanced B removal by Si–Sn–Cu ternary solvent refining with Zr addition

Enhancing P removal from primary Si by P-containing Al2Si2Sr phase during Al–Si solvent refining

Enhanced boron removal by CrMnFeNi-based high-entropy alloys during purification of silicon

Effect of impurity phase migration on Al-30wt.%Si solvent refining with Zr additions during directional solidification

Effect of Si Content on the Morphology Evolution of the Si Primary Dendrites in Al-Si Alloy Solvent Refining Process

Super-gravity field assisted homogeneous distribution of sub-micron eutectic Si in Al-Si alloy

Purification of metallurgical-grade silicon using Si–Sn alloy in presence of Hf, Zr, or Ti

Refinement of Primary Si Phase in Hypereutectic Al–Si Alloy by Electrically Assisted Solidification with P Addition

Purification of metallurgical-grade silicon using zirconium as an impurity getter

Removal of Impurities from Metallurgical Grade Silicon During Ga-Si Solvent Refining

Separation of Al-Si-Fe-(Mn/Cr) melts for simultaneous recycle of Al-Si scraps and purification of silicon

P removal from Si by Si-Ca-Al alloying-leaching refining: Effect of Al and the CaAl2Si2 phase

Effect of Silicon on Precipitates of High-Silicon Austenitic Stainless Steel

Simultaneous preparation of high-purity silicides, eutectic Si/MSi2 (M: Nb, Ta, Mo, or W) alloys, and silicon through the separation of Si–M solvents using electromagnetic directional crystallization

Refinement of primary Si in Al–20%Si alloy by MRB through phosphorus additions

Effect of strontium and melt purification on the solidification microstructure of hypereutectic Al-Si alloys