Abstract:Water-line corrosion is a highly concentrated type of localized corrosion. The conventional single electrode method is limited in its ability to obtain the kinetic information of the corrosion occurrence and development processes. Herein, the coating deterioration and underlying metal corrosion processes in water-line area were studied by a small wire beam electrode to monitor the current density distribution. The distance between each electrode was very small (interval: 0.3 mm), thus facilitating it to approach the practical metal component with a continuous surface. The results showed that cathodic and anodic sites tended to be weak points of the coating at the initial stage. With the continuous degradation of the coating, the cathodic zone tended to occur in the above the anodic zone due to the effect of differential aeration cells (DACs). Subsequently, the cathodic zone expanded to the waterline and the polarity reversed to the anodic zone, causing the coating to peel and blister continuously from the bottom up. When the cathodic zone extended to the gas phase area above the water line, this area became the strongest cathodic zone under the action of the thin liquid film, thus significantly accelerating the corrosion of the base metal at the bottom. The present study aims to achieve an in-depth understanding of coating deterioration and underlying metal corrosion processes in the water-line area, providing a new means of directly visualizing the role of DACs played in water line corrosion.

What problem does this paper attempt to address?

This paper attempts to address the complex mechanisms involved in the degradation of coatings and the corrosion of base metals in the waterline area. Specifically, the authors focus on how to monitor and understand the processes of coating degradation and localized uneven corrosion of base metals in the waterline area through experimental methods such as the Wire Beam Electrode (WBE) technique, particularly under the influence of Differential Aeration Cells (DACs). ### Background of the Paper Water-Line Corrosion (WLC) is a highly concentrated localized corrosion phenomenon that typically occurs at the gas-liquid-solid three-phase interface. Traditional single-electrode methods have limitations in obtaining kinetic information about the occurrence and development of corrosion. Therefore, researchers need a new method to directly observe and analyze the processes of coating degradation and base metal corrosion in the waterline area. ### Research Objectives 1. **Understanding the mechanisms of coating degradation and base metal corrosion**: Using the Wire Beam Electrode (WBE) technique to monitor current density distribution, study the degradation process of coatings in the waterline area, and the corrosion process of base metals. 2. **Revealing the role of Differential Aeration Cells (DACs)**: Investigate the role of DACs in waterline corrosion, particularly how they affect the dynamic processes of coating degradation and base metal corrosion. 3. **Providing new research methods**: Offer a new, direct visualization method for studying coating degradation and base metal corrosion in the waterline area to better understand and control this complex corrosion phenomenon. ### Main Findings 1. **Initial Stage**: In the first few days, the coating effectively protected the base metal, with no significant localized high anodic or cathodic currents, indicating that water and aggressive ions had not yet penetrated the surface of the base metal. 2. **Water Penetration Stage**: As water and aggressive ions penetrated, certain areas of the coating began to show cathodic and anodic points, forming localized corrosion cells. 3. **Coating Peeling and Blistering**: With continuous degradation of the coating, the cathodic area gradually expanded upwards, and the anodic area expanded downwards. When the cathodic area extended to the gas phase area above the waterline, this area became the strongest cathodic region, significantly accelerating the corrosion of the base metal. 4. **Changes in Current Density**: Through vector sum analysis of single-line current density, it was found that the expansion of cathodic and anodic areas led to a gradual increase in the maximum single-line cathodic and anodic currents. Particularly in the thin liquid film area near the waterline, the rate of cathodic reactions significantly increased, leading to a sharp rise in current density. ### Conclusion This study successfully monitored and analyzed the processes of coating degradation and base metal corrosion in the waterline area using the Wire Beam Electrode technique, revealing the important role of Differential Aeration Cells (DACs) in this process. These findings are significant for developing coating materials resistant to waterline corrosion and optimizing evaluation methods.

Coating Deterioration and Underlying Metal Corrosion Processes in Water-Line Area: Role of DACs

Visualizing and understanding corrosion evolution beneath a condensed droplet using the multi-electrode array

Research Progress in Degradation Process of Anti-corrosion Coatings in Water Containing Environments

Corrosion Behavior of Chromium-Free Dacromet Coating in Seawater

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film

Study on mechanism of differential concentration corrosion

Comparison of cathodic protection processes of 40% zinc-rich coatings under immersion and atmospheric conditions: Protection for defective areas

Influence of the composition of working fluids on flow-accelerated organic coating degradation: Deionized water versus electrolyte solution

Multiscale characterization of seawater pipe erosion of B10 copper-nickel alloy welded joints

Characteristics and Evolution of Thin Layer Electrolyte on Pipeline Steel under Cathodic Protection Shielding Disbonded Coating

Study of corrosion behavior of carbon steel under seawater film using the wire beam electrode method

Study on the localized flow-accelerated corrosion of EH32 steel based on wire beam electrodes and EIS measurements

Corrosion Monitoring Techniques in Subcritical and Supercritical Water Environments

Mechanical-Chemical Coupling Effects on an Environmental Barrier Coating System under High-Temperature Water Vapour Conditions

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Electrochemical Measurements Using Combination Microelectrode in Crevice Simulating Disbonded of Pipeline Coatings under Cathodic Protection

Comparative Studies on the Deterioration Process of Organic Coatings under Immersed and Cyclic Wet-Dry Conditions by EIS

The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements

Corrosion of Copper, Cupronickel, Nickel Aluminium Bronze and Super-Duplex Stainless Steel Rotating Cylinder Electrodes in Seawater under Turbulent Flow Conditions

Electrochemical Study on Corrosion Damage of 7B04 Aluminum Alloy/Anodic Film/Epoxy Coating System in Simulated Marine Atmospheric Environment

Corrosion self-diagnosing and self-repairing polymeric coatings based on zeolitic imidazolate framework decorated hydroxyapatite nanocontainer on steel