Abstract:<p>CFRP has been gradually used in the load-carrying structure with thicker component and stricter damage tolerance in aviation industry. However, the heat accumulation always occurs at hole exit-ply during thick CFRP drilling, resulting in temperature even higher than the glass transition temperature (<em>T<sub>g</sub></em>) of matrix, affected by which severe damages will occur based on an unknown cutting mechanism. Therefore, to investigate the new mechanism, this paper proposed a temperature controlled orthogonal cutting experiment by heating the cutting area to specified high temperature ranges (below and above <em>T<sub>g</sub></em>) before cutting. The results show that the resin matrix will be only softened by the high temperature below <em>T<sub>g</sub></em> and lose part of its strength, but the cutting mechanism is almost not changed. As for temperature above <em>T<sub>g</sub></em>, the resin matrix will be heated into molten state thereby losing the support function for machined fibers, which changes the cutting mechanism at 90° <<em>θ</em> <180° into low efficiency cutting mode controlled by compressing stress. The fibers that lose support will be over bent and broken by flank face, and severe thermal mechanical damages including loose face, matrix cracking and fiber pull out can be captured at <em>θ∼</em>150° of hole wall near exit.</p>
What problem does this paper attempt to address?
The problems that this paper attempts to solve are as follows: In the aviation industry, as carbon - fiber - reinforced polymers (CFRP) are gradually used to manufacture load - bearing structures (such as fuselage panels and central wing boxes), these structural components become thicker and the requirements for damage tolerance are more stringent. However, during the drilling process of thick CFRP, due to the accumulation of cutting heat, the temperature at the hole exit may rise above the glass - transition temperature (\(T_g\)) of the matrix, resulting in severe thermo - mechanical damage. Therefore, in order to explore this unknown cutting mechanism, this study designs a temperature - controlled orthogonal cutting experiment to investigate the influence of different temperature ranges (below and above \(T_g\)) on the CFRP cutting mechanism.
Specifically, this study aims to:
1. **Explore the influence of high temperature on the CFRP cutting mechanism**: In particular, how high temperature changes the cutting mechanism and the resulting damage mechanism under different fiber - cutting angles (FCA).
2. **Evaluate the cutting behavior and damage mechanism in different temperature ranges**: Verify the softening degree of the resin matrix at different temperatures and its influence on the cutting process through experiments.
3. **Reveal the reasons for the decline in the quality of the hole exit**: How high temperature reduces the performance of the matrix, thereby affecting the quality of the hole exit, including damages such as loose surfaces, matrix cracking, and fiber pull - out.
To solve these problems, the author designs and implements a temperature - controlled orthogonal cutting experiment. By heating the cutting area to the specified high - temperature range (below and above \(T_g\)), then conducting cutting experiments, and analyzing the chip - formation mode and sub - surface damage mode. The experimental results show that when the temperature is below \(T_g\), the resin matrix will soften but the cutting mechanism hardly changes; when the temperature is above \(T_g\), the resin matrix will melt, losing the function of supporting the fibers, resulting in the cutting mechanism changing to an inefficient compressive - stress - controlled mode and causing severe thermo - mechanical damage.
### Key Formulas and Symbols
- \(T_g\): Glass - transition temperature
- \(F_c\): External load
- \(\sigma_0\): Compressive stress along the fiber direction
- \(\tau_{po}\): Planar shear stress in the uncut layer
- \(\sigma_{90}\) and \(\tau_{90}\): Compressive stress and shear stress in the uncut layer
- \(F_\sigma\) and \(F_\tau\): Two components of the external load \(F_c\), respectively along the fiber direction and perpendicular to the fiber direction
Through these experiments and analyses, the researchers hope to better understand the influence of high temperature on the CFRP cutting mechanism, thereby optimizing the processing technology and reducing the damage at the hole exit.