Abstract:In situ investigation of chemical vapor deposition (CVD) is of critical importance to understanding growth mechanisms of transition-metal dichalcogenides (TMDs) and to develop technologies for growing high-quality monolayer single crystals. However, the in situ investigation is still a great challenge in practice, because TMD CVD growth is conducted at a high temperature with a reduction environment. In this work, we developed an in situ investigation system for CVD growth and presented real-time observations of monolayer MoS2 deposition on the SiO2/Si substrate. We discovered that monolayer MoS2 should be grown via the vapor-state precursor reaction and crystallized from the prenucleation sites on a substrate, an intermediate-phase MoO2 was essential for the nucleation seeding, but the population density should be controlled, and a high-concentration S vapor promoted the in-plane epitaxial growth of MoS2; hence, it was of great benefit to obtain a high-quality monolayer with a compact shape.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaelm.0c00231.Figure S1. Schematic representation of MoS2 CVD growth in a microfurnace; Figure S2. Sulfurization process of 2D MoO3 flakes with the thickness of 6 nm; Figure S3. Raman characterization of monolayer MoS2 grown via two modes; Figure S4. Characterization of the MoO2 film sulfurized by the high-temperature S vapor; Figure S5. High-quality monolayer MoS2 growth using the microfurnace under in situ observations (PDF)Movie S1. MoO3 sublimation (MPG)Movie S2. In situ observation of MoS2 growth (MPG)Movie S3. In situ observation of MoO2 deposition (MPG)Movie S4. Monolayer MoS2 growth vs MoO2 deposition (MPG)Movie S5. Monolayer MoS2 growth and roughing (MPG)This article has not yet been cited by other publications.

Effect of temperature on the growth of two-dimensional MoS2 on low-cost soda-lime glass

Chemical Vapor Deposition of Uniform and Large-Domain Molybdenum Disulfide Crystals on Glass/Al2O3 Substrates

Chemical Vapor Deposition Of Large-Size Monolayer Mose2 Crystals On Molten Glass

Effect of growth temperature on the morphology control and optical behavior of monolayer MoS2 on SiO2 substrate

Scalable growth of atomically thin MoS2 layers in a conventional MOCVD system using molybdenum dichloride dioxide as the molybdenum source

Low-temperature synthesis of uniform monolayer molybdenum disulfide films

Scalable growth of atomically thin MoS 2 layers in a conventional MOCVD system using molybdenum dichloride dioxide as the molybdenum source

Highly Efficient Deposition of Centimeter-Scale MoS2 Monolayer Film on Dragontrail Glass with Large Single-Crystalline Domains

Ultrafast Growth of Large‐Area Uniform, Millimeter‐Size MoSe 2 Single Crystals on Low‐Cost Soda‐Lime Glass

Ultrafast Growth of Large‐Area Uniform, Millimeter‐Size MoSe2 Single Crystals on Low‐Cost Soda‐Lime Glass

Substrate-induced strain in molybdenum disulfide grown by aerosol-assisted chemical vapor deposition

Space-confined CVD Growth of 2D-Mos2 Crystals with Tunable Dimensionality Via Adjusting Growth Conditions

Synthesis of High-Performance Monolayer Molybdenum Disulfide at Low Temperature.

Importance of the Substrate's Surface Evolution During the MOVPE Growth of 2D-Transition Metal Dichalcogenides.

Large‐Size Monolayer MoSe 2 Single Crystals: Ultrafast Growth of Large‐Area Uniform, Millimeter‐Size MoSe 2 Single Crystals on Low‐Cost Soda‐Lime Glass (Adv. Mater. Interfaces 12/2021)

High-Temperature In Situ Investigation of Chemical Vapor Deposition to Reveal Growth Mechanisms of Monolayer Molybdenum Disulfide

Large Area Vapor Phase Growth and Characterization of MoS2 Atomic Layers on SiO2 Substrate

Wafer-scale MOCVD growth of monolayer MoS2 on sapphire and SiO2

Oxygen-Assisted Chemical Vapor Deposition Growth of Large Single-Crystal and High-Quality Monolayer MoS2.

Effect of Process Temperature on Molybdenum Disulphide Layers Grown by Chemical Vapor Deposition Technique

Effect of MoO3 Vapor Flow to Large Area MoS2 Few-Layered Films Growth