Temperature-dependent diffuse reflectance measurements of ceramic powders in the near- and mid-infrared spectra

J. Michael Mayer,James A. Abraham,Brandon Surhigh,Bryan Kinzer,Rohini Bala Chandran

DOI: https://doi.org/10.1016/j.solener.2022.08.071

IF: 7.188

2022-10-01

Solar Energy

Abstract:Radiative properties are critical to quantify radiative energy fluxes between surfaces and in participating media. However, there is limited experimental data on temperature-dependent radiative properties of materials. This work focuses on experimentally measuring temperature-dependent diffuse reflectance in the near- and mid-infrared spectra (1–20 μm) for ceramic particles with applications as heat-transfer and thermal-storage media in concentrated solar power (CSP) plants. Specifically, a commercially available sintered bauxite proppant, ACCUCAST ID80, and its primary chemical constituents—alumina (Al2O3) and silica (SiO2)—are measured in powder form using a Fourier transform infrared spectrometer (FTIR) coupled with a specialized diffuse reflectance accessory and a heated stage. Room-temperature diffuse reflectance measurements show increased absorption in tests with greater mass fractions of the ceramic samples. There is a strong correlation in the measured reflectance spectra of ACCUCAST with alumina and silica in the spectral range 2000–500 cm−1 (5–20 μm). Whereas, for shorter wavelengths (<5μm), the absorptance for ACCUCAST is greater than the absorptance for alumina and silica, indicating contributions from other chemical species present in the composite material. For the first time, temperature-dependent diffuse reflectance measurements are reported for ACCUCAST up to 1000 °C. These results are compared against those of alumina and silica through the calculation of a thermal emittance. All three materials exhibit a calculated emittance of ∼0.9 at room temperature. However, this value decreases to ∼0.6 for ACCUCAST and drops to less than 0.4 for alumina and silica at 1000 °C. Thermal cycling in air at 1000 °C resulted in a visible color change from dark grey to light orange for ACCUCAST and a subsequent larger increase in reflectance for wavelengths less than 5 μm as compared to ACCUCAST thermally cycled at 1000 °C in vacuum. Alumina and silica spectra proved to be largely unaffected by thermal cycling under atmospheric conditions. Overall, this study establishes a powerful technique for the characterization of radiative properties of particulate materials as a function of temperature and presents a detailed case study of ACCUCAST, a candidate for next-generation particle-based CSP.

energy & fuels