Abstract:CdS thin films have been successfully electrodeposited by introducing oxalic acid in the electrolytic solution as a novel complexing agent to prevent sulfide precipitation. The CdS films were grown on an FTO/glass substrate at − 0.890 V for 10 min and then annealed at 120 °C and 400 °C, respectively, in air. X-ray diffraction revealed that the CdS films have mixed hexagonal and cubic phases with (311) cubic-CdS preferred orientation. Scanning electron microscopy (SEM) results illustrated a transition from compact grains with more spherical precipitations on the surface at 120 °C to denser and homogeneous structure with a large crystallite size at 400 °C. The energy dispersive spectroscopy (EDS) revealed a decrease in the S content and an under-stoichiometric composition of CdS film at 400 °C. The band gap value decreased from 2.47 to 2.24 eV as the annealing temperature increased, while optimum transmittance was obtained at 120 °C. Mott–Schottky analysis revealed n-type conductivity for both samples where the flat band potential and donor density vary with the annealing temperature from − 0.99 to − 1.02 V and from 3.9 × 10 20 to 1.1 × 10 21 cm −3 , respectively. The electrochemical impedance studies affirmed that the electrochemical process is under kinetic control and demonstrated lower R CT at 400 °C. PEC measurements showed enhancement in the V OC and J SC at 400 °C, indicating improved sensitivity and efficiency for photodetection. The slow decay of dark and photocurrent was attributed to defects and local potential fluctuations within the films. These findings highlight the effectiveness of using oxalic acid in the deposition process of CdS thin films making them suitable for solar cell applications.

Photocurrent enhancement of spin coated CdS thin films by adding Cu

Improved Performance of Dye Sensitized Solar Cells Using Cu-doped TiO2 As Photoanode Materials: Band Edge Movement Study by Spectroelectrochemistry

Structural And Photoelectrochemical Properties Of Cu-Doped Cds Thin Films Prepared By Ultrasonic Spray Pyrolysis

Structural and electrical properties of CdS thin films spin coated on glass substrates

Optical properties of spin coated and sol-gel dip coated cupric oxide thin films

Chemical synthesis of Cu(In) metal inks to prepare CuInS2 thin films and solar cells

Influence of Cu doping on physical and photo-electrochemical properties of CdS thin films prepared by RF magnetron sputtering

Synthesis of Nanocrystalline CdS:Sn Film and Study on Its Optical, Structural, and Electrical Characteristics

Introduction of Co atoms into CdS thin films for improving photovoltaic properties

Copper effect on cadmium sulfide thin films for spintronics: microstructures, morphological, photoluminescence and magnetic properties

Cu-doped CdS and its application in CdTe thin film solar cell

To Study the Cadmium Sulphide Thin Films Synthesis by Simple Spin Coating Method for Energy Application

Improvement of the photoelectrical properties of chemical bath-deposited Sb2S3 thin films with low copper doping

Effect of cadmium concentration on the structural, morphological, and optical properties of ZnS nanoparticles

Preparation and characterization of CdS prepared by hydrothermal method

Effect of annealing treatment on oxalic acid-assisted electrodeposited CdS thin films for enhanced solar cell performance

Preparation and Characterization of CdS by Evaporation and Cu2S Complex Photoelectric Thin Films

Optical Transmission, Photoconductivity, and Morphology of Chemical Bath-Deposited CdS Thin Films for Optoelectronic Applications

Effect of copper doping on plasmonic nanofilms for high performance photovoltaic energy applications

Optical Properties of CuCdS Thin Film Prepared by Vacuum Thermal Evaporation Technique

Recent developments and prospects of copper tin sulphide (Cu 2 SnS 3 ) thin films for photovoltaic applications