Abstract:Phase equilibria and structural transformations in the ternary ZrO2–HfO2–Eu2O3 system at 1100 °C were studied by X-ray diffraction over the entire composition range. The samples of different compositions have been prepared from nitrate acid solutions by evaporation, drying, and calcinations at 1100 °C. Fields of solid solutions based on the cubic (F) modification with fluorite-type structure and tetragonal (T) and monoclinic (M) modifications of ZrO2 (HfO2), cubic (C) modification of Eu2O3, and an ordered intermediate phase with pyrochlore-type structure, Ln2Zr2O7 (Ln2Hf2O7)(Py), were established to exist in the system. The solubility of Eu2O3 in M-HfO2(ZrO2) is pretty low and approximately less than 1 mol%, which is confirmed by XRD. The boundaries of phase fields and lattice parameters of the phases were determined. The lattice parameters for F phase vary from а = 0.5305 nm in two-phase sample (C+F) containing 6.75 mol% ZrO2–8.25 mol% HfO2–85 mol% Eu2O3 to а = 0.5283 nm for sample containing 27 mol% ZrO2–33 mol% HfO2–40 mol% Eu2O3 and to а = 0.5275 nm in two-phase sample (Py+F) containing 29.25 mol% ZrO2–35.75 mol% HfO2–35 mol% Eu2O3, and from а = 0.5232 nm in two-phase sample (Py+F), containing 32.625 mol% ZrO2–39.875 mol% HfO2–27.5 mol% Eu2O3 to а = 0.5218 nm sample containing 33.75 mol% ZrO2–41.25 mol% HfO2–25 mol% Eu2O3 and to а = 0.5176 nm in two-phase sample (F+M) containing 40.5 mol% ZrO2–49.5 mol% HfO2–10 mol% Eu2O3 along the section Eu2O3–(55 mol% HfO2–45 mol% ZrO2). The fluorite-type structure (F) is in equilibrium with all phases that exist in the ternary ZrO2–HfO3–Eu2O3 system at 1100 °C and forms substitutional solid solutions with phases of the binary systems. In the ZrO2–HfO2–Eu2O3 system, an infinite series of solid solutions form from the Ln2Zr2O7 (Ln2Hf2O7) (Py) phase. The isothermal section of the ZrO2–HfO2–Eu2O3 phase diagram at 1100 °C contains one three-phase regions (T + M + F) and six two-phase regions (F + C, two-F + Py, F + M, F + T, T + M). No new phases were found in the ZrO2–HfO2–Eu2O3 system at 1100 °C and the nature of phase equilibria was determined by the constitution of the boundary binary systems.

Phase Equilibria in Low-Temperature Regions of Phase Diagrams

Low Temperature X-Ray Diffraction Study On Phase Transitions

Phase stability determination of negative thermal expansion silicates by theory and experiment

Phase Diagrams of Superconducting Materials

On Low-Temperature Structural Phase Transitions

ISOTHERMAL SECTION OF THE ZrO2–HfO2–Eu2O3 SYSTEM PHASE DIAGRAM AT 1100 °C

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Solid-solid phase equilibria in the NaCl-KCl system

Measurement of the phase equilibria in the Al–Zr–Y system at 673 and 823 K

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Phase equilibria in the ZrO2–YO1.5–NbO2.5 system at 1300°C and high‐temperature experiments in the ZrO2–YNbO4 subsystem

Phase Separation Sequence and Its Effect on Subsequent Crystallization in Cu12.5ni10zr41ti14be22.5 Amorphous Alloy, As Probed by Small-Angle-Neutron Scattering

The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C

Phase Equilibria of the System La2O3–NiO–Li2O at 700, 800, and 900°C

Phase Equilibria of the Sn–Zn–Cu Ternary System

Phase equilibria in the La2O3-Sm2O3-ZrO2 system: Experimental studies and thermodynamic modeling

Phase Equilibria in the Ni-Sn-Zn System at 500°C

Experimental determination of phase diagram in the Zn-Fe binary system

Phase diagram analysis and crystal growth of solid solutions Ca_{1-x}Sr_xF_2

Tuning the low-temperature phase behavior of aqueous ionic liquids

Phase equilibria studies in the CaO–SiO 2 –Al 2 O 3 –MgO system with CaO/SiO 2 ratio of 0.9