Abstract:Phase equilibria and structural transformations in the ternary ZrO2–HfO2–Eu2O3 system at 1100 °C were studied by X-ray diffraction over the entire composition range. The samples of different compositions have been prepared from nitrate acid solutions by evaporation, drying, and calcinations at 1100 °C. Fields of solid solutions based on the cubic (F) modification with fluorite-type structure and tetragonal (T) and monoclinic (M) modifications of ZrO2 (HfO2), cubic (C) modification of Eu2O3, and an ordered intermediate phase with pyrochlore-type structure, Ln2Zr2O7 (Ln2Hf2O7)(Py), were established to exist in the system. The solubility of Eu2O3 in M-HfO2(ZrO2) is pretty low and approximately less than 1 mol%, which is confirmed by XRD. The boundaries of phase fields and lattice parameters of the phases were determined. The lattice parameters for F phase vary from а = 0.5305 nm in two-phase sample (C+F) containing 6.75 mol% ZrO2–8.25 mol% HfO2–85 mol% Eu2O3 to а = 0.5283 nm for sample containing 27 mol% ZrO2–33 mol% HfO2–40 mol% Eu2O3 and to а = 0.5275 nm in two-phase sample (Py+F) containing 29.25 mol% ZrO2–35.75 mol% HfO2–35 mol% Eu2O3, and from а = 0.5232 nm in two-phase sample (Py+F), containing 32.625 mol% ZrO2–39.875 mol% HfO2–27.5 mol% Eu2O3 to а = 0.5218 nm sample containing 33.75 mol% ZrO2–41.25 mol% HfO2–25 mol% Eu2O3 and to а = 0.5176 nm in two-phase sample (F+M) containing 40.5 mol% ZrO2–49.5 mol% HfO2–10 mol% Eu2O3 along the section Eu2O3–(55 mol% HfO2–45 mol% ZrO2). The fluorite-type structure (F) is in equilibrium with all phases that exist in the ternary ZrO2–HfO3–Eu2O3 system at 1100 °C and forms substitutional solid solutions with phases of the binary systems. In the ZrO2–HfO2–Eu2O3 system, an infinite series of solid solutions form from the Ln2Zr2O7 (Ln2Hf2O7) (Py) phase. The isothermal section of the ZrO2–HfO2–Eu2O3 phase diagram at 1100 °C contains one three-phase regions (T + M + F) and six two-phase regions (F + C, two-F + Py, F + M, F + T, T + M). No new phases were found in the ZrO2–HfO2–Eu2O3 system at 1100 °C and the nature of phase equilibria was determined by the constitution of the boundary binary systems.

Phase equilibria in the ZrO2–YO1.5–NbO2.5 system at 1300°C and high‐temperature experiments in the ZrO2–YNbO4 subsystem

Phase equilibria in the ZrO 2 –Ta 2 O 5 –Nb 2 O 5 system: Experimental studies and thermodynamic modeling

Phase equilibria in the ZrO2-GdO1.5-TaO2.5 system at 1500 °C

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Phase equilibria in the La2O3-Sm2O3-ZrO2 system: Experimental studies and thermodynamic modeling

ISOTHERMAL SECTION OF THE ZrO2–HfO2–Eu2O3 SYSTEM PHASE DIAGRAM AT 1100 °C

17O NMR Studies of Local Structure and Phase Evolution for Materials in the Y2Ti2O7–ZrTiO4 Binary System

Fluorite-pyrochlore-weberite phase transitions in a series of 20-component ultrahigh-entropy compositionally complex ceramics

Phase equilibria in the TiO2–Nb2O5 system: New experiments and thermodynamic modeling

Phase Equilibria of the System La2O3–NiO–Li2O at 700, 800, and 900°C

Phase Behaviors of the Zrmo2-Xwxo8 (X=0.2-2.0) System and the Preparation of an Mo-Rich Cubic Phase

The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C

Phase composition, microstructure and thermophysical properties of the Srx(Zr0.9Y0.05Yb0.05)O1.95+x ceramics

Phase Relationship of the TbO1.81–Mn3O4–Fe2O3 System Synthesized at 1200°C

Phase Equilibrium Investigations and Thermodynamic Study of the Y2O3-Ta2O5 System

Phase equilibrium investigations of the Al2O3–Ta2O5 system: New experiments and thermodynamic modeling

Phase Equilibria of the Ternary Ni-Cr-Zr System and Interfacial Reactions in the Ni-Cr/Zr Couples

Thickness Dependence of the Crystallization and Phase Transition in ZrO 2 Thin Films

Experimental Investigation and Thermodynamic Assessment of the Mo–Ni–Zr Ternary System

Phase equilibria in the CaO-TaO2.5-YO1.5 system and its implication for YTaO4 reactivity with CMAS