Abstract:The development of one-part geopolymer mortars has greater potential than the traditional two-part mortars, especially in repair applications, to convert waste into useful beneficial products while simultaneously eliminating the hazards associated with the alkaline solutions. Nevertheless, the inherent brittleness exhibited by the one-part geopolymers displays drawbacks like OPC when subjected to flexural loading. The fibers selection as well as their strengthening effects from literature is considerably scarce, especially for the repairing geopolymer system. This work aims to investigate the influences of fiber types and volume fractions on the workability, physical behavior, and cracking/fatigue resistance of ambient air-cured one-part geopolymer mortar. Reaction kinetics, mineralogical phases, and elemental components were explored by means of the TAM, quantitative XRD, and EDS mapping analysis. The FESEM and X-CT were employed to compare the microstructures and pore characteristics of the fibers-reinforced products. The results show that the copper-plated steel fiber produced the least change in workability, while the basalt fiber produced the lowest flow values. Setting time was the shortest for the basalt fiber reinforced, followed by polyvinyl-alcohol fiber. The steel fiber and carbon fiber would improve the mechanical properties of mortar significantly, especially in the early stage. The fatigue strength of 1 vol% carbon fiber reinforced mortar under 2 million cycles loading was the highest (3.72 MPa). The fibers addition a substantial decrease in sphericity and compactness of the pores (high anisotropy) as evidenced by X-CT data. Moreover, three hydration heat processes occurred after water was added to the one-part geopolymer mortar, which included dissolution of Na2SiO3 particles, network degradation, and a second pozzolanic reaction. More crystalline formation occurred over curing time to form gel networks with high stability and generated different bonding modes with various fibers.

Shrinkage and Cracking Performance of PP/PVA Fiber-Reinforced 3D-Printed Mortar

Effect of Fiber on Mechanical Properties of Cement Stabilized Macadam Mixture

Shrinkage and mechanical properties optimization of spray-based 3D printed concrete by PVA fiber

Pore structure, internal relative humidity, and fiber orientation of 3D printed concrete with polypropylene fiber and their relation with shrinkage

Plastic shrinkage and cracking of 3D printed mortar with recycled sand

PVA Fibre Reinforced High-Strength Cementitious Composite for 3D Printing: Mechanical Properties and Durability

Effect of Polypropylene Fibre Addition on Properties of Geopolymers Made by 3D Printing for Digital Construction

Shrinkage and Cracking Properties of Cellulose Fiber–Concrete Composites for 3D Printing by Leveraging Internal Curing

Mechanical Performance Optimization in Spray-Based Three-Dimensional-Printed Mortar Using Carbon Fiber

Dynamic Properties and Fractal Characteristics of 3D Printed Cement Mortar in SHPB Test

Modification effect of nanosilica and polypropylene fiber for extrusion-based 3D printing concrete: Printability and mechanical anisotropy

Rheological behaviors and structure build-up of 3D printed polypropylene and polyvinyl alcohol fiber-reinforced calcium sulphoaluminate cement composites

Influence of Multi-Walled Nanotubes on the Fresh and Hardened Properties of a 3D Printing PVA Mortar Ink

Study on anisotropy of 3D printing PVA fiber reinforced concrete using destructive and non-destructive testing methods

Performance Characteristics of Micro Fiber-Reinforced Ambient Cured One-Part Geopolymer Mortar for Repairing

Factors Influencing the Properties of Extrusion-Based 3D-Printed Alkali-Activated Fly Ash-Slag Mortar

Influence of Recycled Cement Paste Powder on Early-Age Plastic Shrinkage and Cracking of Cement-Based Materials

A new strategy to enhance 3D printability of cement-based materials: In-situ polymerization

The Mechanical Properties of Polymer-cement Mortar

Methods for measuring plastic shrinkage and related cracking of 3D-printed concrete

Comparative Evaluation of the Applicability of 3D Printing Mortar with Different Waste Powders