Optical properties (uv-vis and ftir) of gamma irradiated polymethyl methacrylate (pmma)

V. N. Rai,C. Mukherjee,Beena Jain

DOI: https://doi.org/10.48550/arXiv.1611.02129

2016-10-27

Abstract:The effect of gamma irradiation on the UV-Vis and FTIR spectroscopy of polymethyl methacrylate (PMMA) foils has been studied. A new absorption band is observed in the visible spectral range due to color centers induced in the gamma irradiated PMMA. This band shows maximum absorption (low transmission) for 10 kGy irradiation, which decreases and saturates after 50 kGy followed by a further increase at 500 kGy. The FTIR peaks show an increased absorption up to ~100 kGy irradiation, which reverses for higher doses. Broad band absorption is observed in FTIR spectra around 1600 and 3600 cm-1 due to absorption of moisture in the irradiated samples. The reduction in the absorption intensity at 1718 cm-1 in the irradiated PMMA (> 100 kGy) is found associated with the demerization of the carbonyl groups. An initial increase in the absorption of FTIR peaks with increase in the doses of irradiation is due to increased cross linking in the PMMA structure that is induced by the absorption of moisture. The demerization of carbonyl groups becomes dominant at higher doses of irradiation (~500 kGy).

Chemical Physics,Soft Condensed Matter

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the effects of γ - ray irradiation on the ultraviolet - visible (UV - Vis) and Fourier - transform infrared (FTIR) spectra of polymethyl methacrylate (PMMA) films. Specifically, the paper focuses on the following aspects:

1. **Generation of color centers**: To study the generation of color centers induced by γ - ray irradiation in PMMA and their influence on optical absorption. Color centers are defects or free radicals in materials caused by radiation, resulting in new absorption bands in the material within a specific wavelength range.

2. **Chain scission and cross - linking**: To explore the effects of γ - ray irradiation on the molecular structure of PMMA, especially the processes of chain scission (C - C bond breakage) and cross - linking (formation of chemical bonds between molecules). These processes will affect the physical properties of PMMA, such as molecular weight and optical transparency.

3. **Depolymerization of carbonyl groups**: To study the depolymerization phenomenon of carbonyl groups (C = O) in PMMA under high - dose γ - ray irradiation. Depolymerization will lead to a reduction in the number of carbonyl groups, thereby affecting the chemical structure and performance of the material.

4. **Moisture absorption**: To analyze the influence of γ - ray irradiation on moisture absorption in PMMA. Irradiation may cause PMMA to absorb more moisture, which in turn will affect certain characteristic peaks in its infrared spectrum.

### Main findings
- **UV - Vis spectrum**: The irradiated PMMA shows new absorption bands in the visible light region (384 - 523 nm), which are attributed to the generation of color centers. The absorption intensity reaches a maximum at 10 kGy, then gradually decreases and saturates between 50 kGy and 100 kGy, and increases again at 500 kGy.
- **FTIR spectrum**: The FTIR spectrum of irradiated PMMA shows new absorption peaks near 1600 cm\(^{-1}\) and 3600 cm\(^{-1}\), which are related to moisture absorption. The absorption peak of carbonyl groups (1718 cm\(^{-1}\)) is enhanced at low - dose irradiation but weakened at high - dose irradiation, indicating the depolymerization phenomenon of carbonyl groups.

### Conclusion
Through the study of UV - Vis and FTIR spectra, the paper reveals the effects of γ - ray irradiation on the optical and structural properties of PMMA films. These results are helpful for understanding the modification mechanism of irradiation on polymer materials and provide theoretical support for the application of polymers in high - radiation environments.