Revealing the effects of electron beam irradiation on the structural, optical, thermal, and dielectric properties of PVC/Ag2WO4 nanocomposite films
M. I. A. Abdel Maksoud,Ramy Amer Fahim,Said M. Kassem,Mohamed Gobara,A. S. Awed
DOI: https://doi.org/10.1007/s11082-024-06472-x
IF: 3
2024-03-04
Optical and Quantum Electronics
Abstract:Herein, rod-like shape of Ag 2 WO 4 was synthesized using the co-precipitation approach. These rods were mixed with PVC using the solution casting process to create a PVC/Ag 2 WO 4 nanocomposite film. The effect of exposing the PVC/Ag 2 WO 4 nanocomposite film to varying doses of the electron beam (E-beam) irradiation (0, 25, 50, and 100) kGy on its structural, optical, thermal, electric modulus, complex impedance, and dielectric properties was investigated. XRD results showed that Ag 2 WO 4 has mixed phases. The optical properties have been addressed. The thermal evaluations were performed at three distinct heating rates: 6, 8, and 10 °C/min. In the same context, the thermal activation energy (E a ) of the unirradiated PVC/Ag 2 WO 4 nanocomposite films increased from 12.89 to 31.17 kJ/mol with the increase in E-beam irradiation doses. As a result, E-beam irradiation reduces the values of the real (ɛ′) and imaginary (ε′′) components of PVC/Ag 2 WO 4 nanocomposite films. The electric modulus analyses showed that the magnitude of the grain capacitance increased as the E-beam doses increased, while the magnitude of the grain boundary capacitance exhibited a decreasing trend. Meanwhile, a progressive reduction in the diameter of the two semicircular arcs for complex impedance analyses was observed as the doses of E-beam irradiation increase.
engineering, electrical & electronic,optics,quantum science & technology