Abstract:Steel wire ropes will creep under long-term loading, resulting in the deterioration of tensile structure performance. From the perspective of materials science, the creep of steel ropes can be understood as the degradation of their equivalent elastic modulus over time, and there are currently no methods or formulas to quantify this degradation. The main purpose of this paper is to propose a general formula for calculating the equivalent modulus degradation of wire ropes, which will facilitate the assessment of performance variations in tensile structures during service. In this study, an experiment on the degradation of the equivalent elastic modulus of steel wire ropes under long-term loading was conducted. In the experiment, measurements were taken using two types of small-diameter steel wire ropes at three stress levels, with data collected over 20,000 h. The results showed that the degradation of the equivalent elastic modulus transitions from rapid to gradual over time and can be divided into three periods. A universal calculation formula was proposed to conveniently express this degradation law, derived from viscoelastic theory with specific parameters obtained through data fitting. To extend the formula's applicability to a wider range of diameters and stress levels, ANSYS was utilized to develop refined models of steel wire ropes and the parameters were determined by the experimental results. After comparison, it was observed that the differences between the calculated values of the formula and the simulated values of the model were relatively small for small diameters, verifying the accuracy of the proposed formula. However, for larger diameters, significant differences were observed in the early phase of the second period. Consequently, an additional experiment was conducted on a wire rope with a diameter of 18 mm to verify the feasibility of the formula for large diameters. The results showed that the measured values closely matched the simulated values from the model. Based on the simulated values, a revised formula was proposed for largediameter ropes. The two proposed calculation formulas can be used to quickly estimate the degradation of the equivalent elastic modulus of steel wire ropes. Numerical results further demonstrated that due to the degradation of the equivalent elastic modulus of wire ropes, the mechanical performance of the structure significantly deteriorates over time, offering a valuable reference for structural health monitoring and tensile structure evaluation.

Cyclic testing of continuously wetted synthetic fiber ropes

Wear mechanisms in polymeric mooring ropes during yarn-on-yarn wear tests

Experimental Evaluation of Dimension-Stable Synthetic Fibre Rope under Investigation of Spooling Test on the Multilayer Winch Drum

The Degradation of Equivalent Elastic Modulus of Steel Wire Ropes under Long-Term Loading

A novel fiber‐reinforced polymer rope: Simulation and theoretical investigation

Experimental measurement for dynamic tension fatigue characteristics of HMPE fibre ropes

Experimental investigation of spooling test on the multilayer oceanographic winch with high-performance synthetic fibre rope

Experimental Characterization of Stiffness of a Polyester Mooring Rope for a CFPSO

Experimental study on cyclic-bend-over-sheave (CBOS) characteristics of an HMPE fibre rope under dynamic loading

Experimental study on the behavior of polyamide multifilament subject to impact loads under different soaking conditions

Experimental evaluation of the main parameters influencing friction between polyamide fibers and influence of friction on the abrasion resistance

A novel fiber-reinforced polymer rope: Concept design and experimental evaluation

Abrasion performance and failure mechanism of fiber yarns based on molecular segmental differences

Basic study for drive mechanism with synthetic fiber rope – investigation of strength reduction by bending and terminal fixation method

The effects of preloading on tensile properties of braided polyarylate fiber ropes

A New Fully-Detailed Finite Element Model of Spiral Strand Wire Ropes for Fatigue Life Estimate of a Mooring Line

Experimental Investigation of Stresses in Winch Drums Subjected to Multilayer Spooling Loads From Synthetic Fibre Ropes

Robust Contact and Friction Model for the Fatigue Estimate of a Wire Rope in the Mooring Line of a Floating Offshore Wind Turbine

Effect of applied sustained load and severe environments on durability performance of carbon-fiber composite cables

Cyclic Testing of Polymer Composites and Textile Cords for Tires

Synthetic Rope Properties and End Connector Concepts For Use in Timber Harvesting Applications