Abstract:The passivation behavior of hydrogen-charged iron-based amorphous alloys ((FexCr13P7C, x=5, 10 and 15) and a nickel-based amorphous alloy (Ni15Cr16P4B) has been investigated in a sulphuric acid solution at 303 K using the electrochemical method. The specimens were first hydrogen charged at a constant current density of 2 × 10−3 A cm−2 for different charging times and immediately were polarized for passivation at a constant potential of 0.445 V SHE−1 on the iron alloys and 0.645 V SHE−1 on the nickel alloy for 1 h in the same solution. For the iron-based amorphous alloys, the passive current and the amount of charge passed during the polarization drastically changed at a charging time of 3–4 h, which was called the crtical charging time. After the critical charging time, the surface changed from shiny to black in color. The black film reduces the corrosion resistance in the sense that it interferes with the passivation. The Ni15Cr16P4B amorphous alloy examined for comparison exhibited no such critical charging time.

The effect of hydrogen on the passivity of iron-based and nickel-based amorphous alloys