Real-time Stress Measurements in Germanium Thin Film Electrodes during Electrochemical Lithiation/delithiation Cycling

Siva P.V. Nadimpalli,Rajasekhar Tripuraneni,Vijay A. Sethuraman
DOI: https://doi.org/10.1149/2.0941514jes
2015-11-08
Abstract:An in situ study of stress evolution and mechanical behavior of germanium as a lithium-ion battery electrode material is presented. Thin films of germanium are cycled in a half-cell configuration with lithium metal foil as counter/reference electrode, with 1M LiPF6 in ethylene carbonate, diethyl carbonate, dimethyl carbonate solution (1:1:1, wt. %) as electrolyte. Real-time stress evolution in the germanium thin-film electrodes during electrochemical lithiation/delithiation is measured by monitoring the substrate curvature using the multi-beam optical sensing method. Upon lithiation a-Ge undergoes extensive plastic deformation, with a peak compressive stress reaching as high as -0.76 +/- 0.05 GPa (mean +/- standard deviation). The compressive stress decreases with lithium concentration reaching a value of approximately -0.3 GPa at the end of lithiation. Upon delithiation the stress quickly became tensile and follows a trend that mirrors the behavior on compressive side; the average peak tensile stress of the lithiated Ge samples was approximately 0.83 GPa. The peak tensile stress data along with the SEM analysis was used to estimate a lower bound fracture resistance of lithiated Ge, which is approximately 5.3 J/m^2. It was also observed that the lithiated Ge is rate sensitive, i.e., stress depends on how fast or slow the charging is carried out.
Materials Science
What problem does this paper attempt to address?