Abstract:Active materials used in lithium ion batteries consist of micro-metric ceramic particles. Mechanical failure can happen within these brittle particles due to large internal stresses provoked by lithium intercalating in the crystalline structure during charge and discharge. Their mechanical behavior is directly related to some key intrinsic parameters, namely the elastic modulus, the fracture toughness and lithium di usivity. This works deals with the development of new characterization techniques to quantify these parameters at the local scale. Obtaining quantitative measurements is notably challenging for this type of specimen due to the highly heterogeneous structure of battery electrodes. For this, spinel LiMn2O4-based commercial cathodes are proposed as material of investigation. First, composition analysis of cathode materials at di erent states of charge was done. In general it was noticed that commercial cells are not as consistent as laboratory cells: impurities are often present (Ni, Co,...) and particles can be porous agglomerates of nanoparticles as well as large single grains. However only spinel structure was detected by X-ray di raction and Rietveld analysis showed a typical lattice expansion for higher lithium concentrations. A method using nanoindentation was developed. It consists of applying a large number of indents in cathode cross-sections and subsequently ltering the measurements depending on whether they t the set of hypotheses of the Oliver and Pharr method. It was observed that for decreasing lithium concentrations, the elastic modulus and the hardness increase from 87 GPa (0% State of Charge) to 104 GPa (100% SoC) and from 7.0 GPa (0% SoC) to 8.0 Gpa (100%SoC), respectively. With the help of contact-resonance atomic force microscopy, the elastic property could also be qualitatively mapped and it seems that the particles are homogeneous. Added to micro-raman spectroscopy, it was observed that neighboring particles can have di erent lithiation levels. The fracture toughness was estimated by measuring the crack opening displacement by atomic force microscopy and applying Irwin’s near eld theory. A toughness of about 0.9 MPa·m was found but should not be taken at face-value. Irwin’s theory requires a purely elastic-brittle fracture with traction-free crack walls. Unfortunately this condition cannot be met due to the size of the particles and the toughness is surely overestimated. Associated with electron backscattered di raction, cleavage planes were also evaluated on a reference {111} wafer. It was found that cracks always propagate in the <121> direction, corresponding to {101} planes just below the surface. At higher depths (> 100 nm), the crack deviates of 30 to 40◦. The last part of this work consists of developing a model to better comprehend electrochemical strain microscopy “time spectroscopy” (ESM-TS). It is the most promising technique to quantify locally ionic di usion coe cients. An AFM cantilever is used

Nanoindentation Size Effects in Lithiated and Sodiated Battery Electrode Materials

(Invited) Understanding the Coupled Electrochemical-Mechanical Behavior of Materials for Improving the Performance and Durability of Lithium-Ion Batteries

Lithiation of SiO2 in Li-ion Batteries: in Situ Transmission Electron Microscopy Experiments and Theoretical Studies.

Nanomechanics of Li-ion battery materials

Quantitative spatiotemporal Li profiling using nanoindentation

Rethinking battery degradation in presence of surface effects: mechanical versus electrochemical peformance mediated by charging condition

Diffusion-Induced Transient Stresses in Li-Battery Electrodes Imaged by Electrochemical Quartz Crystal Microbalance with Dissipation Monitoring and Environmental Scanning Electron Microscopy

Stress-mediated Lithiation in Nanoscale Phase Transformation Electrodes

Mechano-electrochemical and Buckling Analysis of Composition-Gradient Nanowires Electrodes in Lithium-Ion Battery

Combining mechanical and chemical effects in the deformation and failure of a cylindrical electrode particle in a Li-ion battery

Investigation of the Deformation Mechanisms of Lithium-Ion Battery Components Using In-Situ Micro Tests

In Situ Study of Li-ions Diffusion and Deformation in Li-rich Cathode Materials by Using Scanning Probe Microscopy Techniques

Nanoindentation measurements of anisotropic mechanical properties of single crystalline NMC cathodes for Li-ion batteries

Electro-chemo-mechanical behavior of lithium-ion battery electrodes

Cohesive Modeling of Crack Nucleation under Diffusion Induced Stresses in a Thin Strip: Implications on the Critical Size for Flaw Tolerant Battery Electrodes

In Situ Measurement of Mechanical Property and Stress Evolution in a Composite Silicon Electrode

Heterogeneous Effects on Chemo-Mechanical Coupling Behaviors at the Single-Particle Level

Real-time Stress Measurements in Germanium Thin Film Electrodes during Electrochemical Lithiation/delithiation Cycling

Probing Lithium Germanide Phase Evolution and Structural Change in a Germanium-in-Carbon Nanotube Energy Storage System

Electrochemical-Mechanical Coupling Experiments on Solid-State Battery Materials and Interfaces

Stress Effects on Lithiation in Silicon