Abstract:This paper investigates the effect of the variation in alkoxide precursor ratio and templating agent concentration on the production of titanium silicalite (TS-1) through analysis using various physical characterisation techniques. X-ray diffraction showed clear evidence for the MFI zeolite structure and a high degree of crystallinity in all systems. For those materials prepared using a templating agent with ultra low alkali metal content, excellent agreement with previously reported unit cell parameters was obtained. For these same systems, 20% higher specific surface areas were also obtained by nitrogen adsorption. Analysis using an energy dispersive x-ray spectrometer coupled to a scanning electron microscope showed that the product typically contained between 60 and 90% of the titanium in the precursor and some dependence of titanium incorporation on the initial mixture composition was also observed. The results from Raman spectroscopy indicated titanium incorporation into the silicalite framework for all systems. For those materials produced using a templating agent with low alkali metal content, extra-framework anatase titanium dioxide was also identified at moderate Ti : Si mole ratios (>0.03) in the initial mixture. Due to its lower penetration depth, x-ray photoelectron spectroscopy (XPS) was used to characterise the titanium species in the surface layer. The XPS results indicated that a small amount of extra-framework titania was present in the surface of most of the TS-1 samples and the proportion of extra-framework material was observed to increase with both precursor alkali metal content and precursor titanium to silicon ratio.

Parameters affecting the synthesis of titanium silicalite 1

Synthesis of titanium silicalite-1 using amorphous SiO2 as silicon source

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

The synthesis and characterization of titanium silicalite-1

Rapid Synthesis of Small Zeolite Y Crystals in the Absence of Seed Gel

Studies on the synthesis of titanium silicalite, TS-1

Synthesis and characterization of titanium silicalite TS-1 prepared using phosphonium ions

Influence of Synthesis Conditions on the Morphology of Silicalite-1 Zeolite

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Synthesis of High-Performanced Titanium Silicalite-1 Zeolite at Very Low Usage of Tetrapropyl Ammonium Hydroxide

Studies on the crystallization process of titanium silicalite-1 (TS-1) synthesized using tetrapropylammonium bromide as a template

The silanization process for the hydrothermal synthesis of hierarchical titanium silicalite-1

Synthesis of Titanium Silicalite-1 with Small Crystal Size by Using Mother Liquid of Titanium Silicalite-1 As Seed

Low-Cost Synthesis of Titanium Silicalite-1 (TS-1) with Highly Catalytic Oxidation Performance through a Controlled Hydrolysis Process

Synthesis of titanium silicalite-1 (TS-1) zeolite with high content of Ti by a dry gel conversion method using amorphous TiO2–SiO2 composite with highly dispersed Ti species

Synthesis and Characterisation of Hierarchically Structured Titanium Silicalite-1 Zeolites with Large Intracrystalline Macropores

Modeling Crystallization Kinetics:Synthesis of the High Ti/Si Silicotitanium Molecular Sieve

Synthesis, characterization and catalytic properties of low cost titanium silicalite

Synthesis, characterization and catalytic performance of titanium silicalite-1 prepared in micellar media

Effects of process parameters on nonhydrolytic sol-gel synthesis of Ba0.6Sr0.4TiO3 powders