Influence of Ru-addition on thermal decomposition and oxidation resistance of TiAlN coatings
Zhe R. Liu,Li Chen,Yong Du,Shuyan Zhang
DOI: https://doi.org/10.1016/j.surfcoat.2020.126234
IF: 4.865
2020-11-01
Surface and Coatings Technology
Abstract:<p>Doping element into transition metal nitride coatings to optimize their performance against machining has attracted wide research interests. Here, we report the influence of Ru-addition concerning the thermal decomposition and oxidation behavior of TiAlN coatings. Incorporation of Ru results in a structural transformation of cubic Ti<sub>0.46</sub>Al<sub>0.54</sub>N and Ti<sub>0.43</sub>Al<sub>0.50</sub>Ru<sub>0.07</sub>N into mixed cubic and wurtzite Ti<sub>0.34</sub>Al<sub>0.51</sub>Ru<sub>0.15</sub>N. With 5 at.% Ru-addition, a comprehensive improvement both in hardness (from ~29.94 to 33.15 GPa) and in fracture resistance (raising the H<sup>3</sup>/E<sup>2</sup> ratio by ~39.8%) is obtained. However, further addition of Ru leads to a drop in hardness (to ~26.09 GPa) for Ti<sub>0.34</sub>Al<sub>0.51</sub>Ru<sub>0.15</sub>N due to the precipitation of wurtzite-structure AlN. Moreover, Ru-containing coatings exhibit a later occurrence of spinodal decomposition, indicating their better thermal stability in comparison with Ti<sub>0.46</sub>Al<sub>0.54</sub>N. Nevertheless, the Ru-addition accelerates the transformation from anatase to rutile and hence causes the degeneration in oxidation resistance. Additionally, a mixed oxide scale including Al<sub>2</sub>O<sub>3</sub>, RuO<sub>2</sub>, and TiO<sub>2</sub> is formed on the surface of Ti<sub>0.34</sub>Al<sub>0.51</sub>Ru<sub>0.15</sub>N coating at the early stages of oxidation. Both this porous oxide scale and high density of grain boundaries allow the rapid inward diffusion of oxygen, which is also responsible for the inferior oxidation resistance of our Ru-containing coatings. Based on the comprehensive improvement in hardness and thermal stability, the tool life can be improved by ~32% through 5 at.% Ru addition under certain machining condition.</p>
physics, applied,materials science, coatings & films