Low-Energy Electron Diffraction, X-ray Photoelectron Spectroscopy, and CO-Temperature-Programmed Desorption Characterization of Bimetallic Ruthenium−Platinum Surfaces Prepared by Chemical Vapor Deposition

and Gary S. Chottiner,A. Lamouri,D. Scherson,Yu Luo,Y. Gofer

DOI: https://doi.org/10.1021/JP004234G

2001-06-09

Abstract:Low-energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS), and CO-temperature-programmed desorption (TPD) were used to characterize ruthenium-modified Pt(100) surfaces of very high purity and controlled stoichiometry prepared in ultrahigh vacuum (UHV) by irradiating Ru3(CO)12 films condensed on cold Pt substrates at 150 K with X-rays, and subsequent annealing at ca. 620 K. The presence of Ru on Pt(100) lifted the (5 × 20) reconstruction characteristic of the bare clean substrate; however, the reconstruction reappeared as the bimetallic surfaces were briefly annealed to ca. 900 K. Exposure of nonannealed Ru(θRu ≥ 0.22)/Pt(100), where θRu represents the Ru coverage in monolayers, to large exposures of CO at ca. 200 K yielded smaller θCO, as well as TPD peaks with onset desorption temperatures, Tdes(CO), ca. 50 K lower than those observed for bare Pt(100). More strikingly, however, the CO-TPD spectra of CO-saturated Ru(θRu = 0.42)/Pt(100), which had been briefly annealed to 900 K, displa...

Materials Science,Physics,Chemistry