Abstract:Three types of polyacrylonitrile (PAN) were considered in order to investigate the effect of molecular composition and configuration on the formation of conjugated structures during stabilization and the conversion of that to pseudo-graphite sheets after carbonization. The stabilization process was performed in an inert or oxidative atmosphere with a temperature ramp from 180°Cto 280°C. The thermal behavior was studied by differential scanning calorimetry, and the change of chemical groups and conjugated structures was detected by in situ measurement of infrared (Fourier transform infrared) and ultraviolet–visible spectroscopy, respectively. The carbonization process of the stabilized samples was performed using a thermogravimetric analyzer under nitrogen atmosphere in the temperature range of 150°C–1200°C, and Raman spectra were applied to study the pseudo-graphite sheets of the residuals. It is suggested that the introduction of comonomer or the improvement of the isotactic regularity of the polymer chain are helpful to promote the stabilization reactions and accelerate the formation of conjugated structures rather than the extent of conjugation during stabilization in nitrogen. Moreover, they are also beneficial to obtain higher degree of graphitization and larger size of the pseudo-graphite sheets with less structural defects after carbonization. While stabilization is performed in air, atactic PAN copolymer has the highest extent of stabilization among these three PAN samples, but they are extremely close. PAN samples with comonomer or higher isotacticity still show a little advantage in the formation speed of the conjugated structures. After carbonization, PAN with higher isotacticity has the highest carbon yield and graphitization degree and the largest size of pseudo-graphite sheets with least structural defects. In addition, the presence of oxygen during stabilization is contributory to increase the extent of stabilization and generate some bigger conjugated structures, which leads to obtain higher graphitization degree and larger size of pseudo-graphite sheets, but it also brings more structural defects.

Synthesis and spectroscopic characterization of completely isotactic polyacrylonitrile

Fabrication of one dimensional polyaniline nanofibers by UV-assisted polymerization in the aqueous phase.

Study on Kinetics of Controlled/living Radical Polymerization of Acrylonitrile by RAFT Technique

Controlled/Living Radical Polymerization of Acrylonitrile: an Overview

Synthesis and Nonisothermal Reaction of A Novel Acrylonitrile-Capped Poly(Propyleneimine) Dendrimer with Epoxy Resin

Preparation of polyacrylonitrile with improved isotacticity and low polydispersity

Aqueous Photoiniferter Polymerization of Acrylonitrile

SYNTHESIS AND CHARACTERISTICS OF POLYACRYLONITRILE (PAN) NANOFIBER MEMBRANE USING ELECTROSPINNING METHOD

The formation of conjugated structure and its transformation to pseudo-graphite structure during thermal treatment of polyacrylonitrile

Facile Synthesis of Isotactic Polyacrylonitrile via Template Polymerization in Interlayer Space for Dielectric Energy Storage

Effects of NaIO4 treatment on the chemical and physical properties of polyacrylonitrile fibers

Stabilization of Atactic-Polyacrylonitrile under Nitrogen and Air As Studied by Solid-State NMR

A Study on the Synthesis, Characterization and Properties of Polyaniline Using Acrylic Acid As a Primary Dopant. I: Polymerization and Polymer

Tunable 1D and 2D Polyacrylonitrile Nanosheet Superstructures

Icar Atrp Of Acrylonitrile Under Ambient And High Pressure

Polymerization-induced Self-Assembly of Acrylonitrile Via ICAR ATRP

Preparation and Structural Characterization for Polyacrylonitrile/Carbon Nanotubes Composites Treated with Concentrated Nitric Acid

A Metal-Free Method for Ultra-High Molecular Weight Polyacrylonitrile under Dimethyl Sulfoxide

Facile Rapid Synthesis of Polyaniline (PANI) Nanofibers

Synthesis of PAN with adjustable molecular weight and low polydispersity index (PDI) value via reverse atom transfer radical polymerization

Template Based Synthesis of Aligned Polyacrylonitrile Nanofibers Using A Novel Extrusion Method