Abstract:The present investigation deals with designing Fe, Fe–P binary and Fe–P–Si ternary alloys produced by an in-house developed powder metallurgical technique based on ‘Hot Powder Preform Forging’. Proper soaking of preforms at high temperature (1050°C) eliminates iron-phosphide eutectic and brings entire phosphorus into solution in iron. Attempting hot forging thereafter completely eliminates hot as well as cold shortness and thereby helps to form these preforms (alloys) into very thin sheets of 0.5mm. The use of costly hydrogen atmosphere during sintering has been eliminated by the addition of carbon as a reducing agent to form CO gas within the compact by reacting with oxygen of iron powder particles. The glassy ceramic coating applied over the compact serves as a protective coating to avoid atmospheric oxygen attack over the compact held at high temperature. These alloys so formed were subjected to density examination at various stages. Microstructural study has been carried out to estimate the grain size, volume percentage of porosity in the alloys, and uniform distribution of phosphorus and silicon in an iron matrix. X-ray diffraction studies of these alloys revealed the presence of only ferrite as product phase. Addition of alloying elements such as P and Si has improved the resistivity and magnetic properties of iron. Fe–0.07C–0.2O–0.3P–0.5Si alloy showed a resistivity as high as 31.7μΩcm. Coercivity values of the alloys ranged from 0.51 to 1.98Oe. The total magnetic loss of Fe–0.07C–0.2O–0.3P–0.5Si alloy was the lowest (2.03W/kg) amongst the alloys developed owing to its high resistivity combined with its low coercivity. These alloys which are drawn to thin sheets could find their possible application in the manufacturing of transformer cores.

Resource-saving production of Fe-based amorphous alloys from carbothermal reduction of high-phosphorus oolitic iron ore

Fe-based amorphous alloys with superior soft-magnetic properties prepared via smelting reduction of high-phosphorus oolitic iron ore

Clean production of Fe-based amorphous soft magnetic alloys via smelting reduction of high-phosphorus iron ore and apatite

Synchronous enrichment of phosphorus and iron from a high-phosphorus oolitic hematite ore to prepare Fe-P alloy by direct reduction-magnetic separation process

Green and Efficient Utilization of Ferruginous Gibbsite Ore and Ferruginous Manganese Ore by Synergetic Carbothermic Co-Reduction–Magnetic Separation Process

Ductile Fe-Based Amorphous Alloys with High Iron Content

A unique Fe-based soft magnetic alloy and its magnetic softening mechanism

Fe-based Bulk Amorphous Alloys with Iron Contents As High As 82At%

Design and development of powder processed Fe–P based alloys

High performance Fe-based nanocrystalline alloys with excellent thermal stability

Improvement of glass forming ability and soft magnetic properties of Fe-C-Si-P amorphous alloys through a flux treatment technique

Design of Fe-based nanocrystalline alloys with superior magnetization and manufacturability

Advances in Fe-based amorphous/nanocrystalline alloys

A novel process for the direct utilization of copper slag and phosphate rock by compound modification and coreduction

Preparation of FeCo-based amorphous alloys with excellent soft magnetism and high glass transition temperature

Magnetic and Thermal Studies of Iron-Based Amorphous Alloys Produced by a Combination of Melt-Spinning and Ball Milling

The influence of P on glass forming ability and clusters in melt of FeSiBP amorphous soft-magnetic alloy

Effects of P addition on the glass forming ability, crystallization behaviour and soft magnetic properties of FeNi-based amorphous alloy

Direct Reduction of High-Phosphorus Oolitic Hematite: Quantifying Phosphorus Migration and Recovery

Effect of continuous rapid annealing on the microstructure and properties of Fe85P11C2B2 amorphous alloy

Iron Recovery and Dephosphorization Behaviors from High-Phosphorus Oolitic Hematite by Gas-Based Direct Reduction and Magnetic Separation