Improvement of glass forming ability and soft magnetic properties of Fe-C-Si-P amorphous alloys through a flux treatment technique

Qiang Li,Seonghoon Yi

DOI: https://doi.org/10.1007/s12540-014-1001-5

IF: 3.451

2014-01-01

Metals and Materials International

Abstract:Effects of fluxing treatment on the glass forming ability and magnetic properties of Fe-based amorphous alloys prepared using industrial raw materials have been studied. The partially amorphous Fe76Si8P9C7 rod with the diameter of 1 mm was prepared by suction casting technique from the fluxed master alloy based on the industrial raw materials, while the alloy rod with the diameter of 1 mm obtained from the un-fluxed master alloy does not involve any amorphous phase. Melt spun ribbons prepared using the fluxed master exhibited lower the coercivity Hc and power loss than those for ribbons prepared using the un-fluxed master alloy. These beneficial effects should be attributed to the purification of the master alloy through flux treatments. The results reveal that fluxing technique can play an important role in the development of Fe-based bulk metallic glasses using industrial raw materials with relatively low purities.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the glass - forming ability and soft magnetic properties of Fe - C - Si - P amorphous alloys prepared from industrial raw materials by using flux treatment technology. Specifically, the research aims to evaluate the role of flux treatment technology in the development of new Fe - based bulk metallic glasses (BMG), especially in the case of using industrial raw materials in the Fe - Si - P - C alloy system. Since industrial raw materials usually contain a large amount of impurities, these impurities become effective heterogeneous nucleation points during the alloy solidification process, resulting in a decline in the glass - forming ability (GFA) of the alloy. Therefore, these impurities are removed by flux treatment in order to improve the glass - forming ability of the alloy and improve its soft magnetic properties.