Analysis of phase equilibria in liquid chromomanganese steel in the presence of calcium. Report 2. Phase equilibria in the system Fe–Ca–Cr–Mn–C–O (economy-alloy steels).

A. L. Makrovets,I. V. Bakin

DOI: https://doi.org/10.32339/0135-5910-2024-3-12-22

2024-04-12

Abstract:Recently, materials devoted to the behavior of active elements in liquid steel during its out-of-furnace processing have been actively published. The processes of formation of nonmetallic inclusions during the interaction of oxygen with deoxidizers and modifiers (Al, Si, Ca, Ba, etc.) in iron-carbon melts have been studied in sufficient detail. Moreover, in a real metal, the process of deoxidation and modification takes place in the presence of alloying elements, which can noticeably change the composition of the forming phases. To assess the influence of the main alloying elements on the formation of non-metallic inclusions, it seems advisable to carry out work on thermodynamic modeling of the processes taking place in liquid steel in the presence of chromium and manganese. In this work, emphasis is placed on economically alloyed steel grades containing up to 2 (wt.) % of manganese, up to 1.5 (wt.) % chromium and up to 1 (wt.) % carbon. The influence of the content of main alloying elements on the deoxidizing ability of calcium in liquid steel has been studied. Liquid oxide inclusions can form when the chromium content at the level of tenths of a percent, manganese at the level of 0.1 (wt.) % and calcium less than 10–4 (wt.) % (1 ppm). The appearance of calcium chromite as non-metallic inclusions is possible in a narrow range of liquid metal compositions. In the presence of carbon, the formation of an oxide melt as an equilibrium non-metallic phase becomes impossible. At a low calcium content, the formation of calcium chromite and chromium oxides as non-metallic inclusions is most likely, and the residual oxygen content in the liquid metal will be about 0.04 (wt.) % (400 ppm).