Addition of Titanium Oxide Inclusions into Liquid Steel to Control Nonmetallic Inclusions

Miia Kiviö,Lauri Holappa

DOI: https://doi.org/10.1007/s11663-011-9603-5

2011-11-17

Metallurgical and Materials Transactions B

Abstract:Titanium oxide inclusions in steel are well known to inhibit grain growth and act as nucleation sites for acicular ferrite because of absorbing manganese from the surrounding steel resulting in a manganese depleted zone around the inclusion. In this article, the inclusions resulting from TiO2 additions to low-alloyed C-Mn-Cr steel were studied. Different types of TiO2 containing materials were added to liquid steel before or during casting to get small titanium-oxide–rich inclusions in steel. The main goals were to find out what happens to TiO2 in liquid steel after addition and during cooling and to study further what type of inclusions are formed in the steel as a result of the TiO2 addition. Based on the thermodynamic calculations and the results of scanning electron microscope (SEM)-energy dispersive spectroscope (EDS) and SEM-electron backscatter diffraction (EBSD) analysis, TiO2 is first reduced to Ti3O5 in liquid steel at high temperatures and then to Ti2O3 during cooling at around 1573 K (1300 °C). Both reactions liberate oxygen, which reacts with Ti, Mn, and Al forming complex Ti2O3-rich inclusions. The results also show that TiO2 additions result in more TiOx + MnO inclusions compared with experiments with Ti addition and that the absolute amount of manganese present in the inclusions is much higher in experiments with TiO2 addition than in experiments with Ti additions.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to solve the problem of controlling non - metallic inclusions by adding titanium dioxide (TiO\(_2\)) to liquid steel. Specifically, the research objectives include:

1. **Understanding the behavior of TiO\(_2\) in liquid steel**: Explore what changes will occur to TiO\(_2\) after it is added to liquid steel at high temperatures and during the cooling process.
2. **Studying the types of inclusions formed**: Analyze the specific types and distribution of inclusions formed in steel after adding TiO\(_2\).
3. **Optimizing the properties of inclusions**: By adding different types of TiO\(_2\) materials, attempt to generate fine and uniformly distributed titanium - rich oxide inclusions to control the grain size and promote the formation of acicular ferrite.

Through experiments and thermodynamic calculations, the paper reveals the reduction process of TiO\(_2\) in liquid steel and its influence on the formation of inclusions. The main findings include:
- TiO\(_2\) is first reduced to Ti\(_3\)O\(_5\) at high temperatures and then further reduced to Ti\(_2\)O\(_3\) when cooled to about 1573 K (1300°C).
- The oxygen released by these reactions will react with Ti, Mn and Al to form complex Ti\(_2\)O\(_3\)-enriched inclusions.
- After adding TiO\(_2\), more TiO\(_x\)+MnO inclusions are formed in the steel, and the absolute content of manganese in the inclusions is significantly higher than that in the case of adding only Ti.

These results are helpful for understanding the mechanism of action of TiO\(_2\) in steel and provide a theoretical basis for improving the properties of steel by controlling inclusions.