Abstract:The aim of this study is to enhance the plasticity and strength of M2 high-speed steel through electron beam melting (EBM) technology. Therefore, by controlling different melting times to change the energy input, a gradient distribution of grain size and uniform distribution of carbides can be achieved. During the deformation process, the gradient structure causes geometrically necessary dislocations (GND) to accumulate near the boundary of regions in the soft zone, resulting in compressive stress in the soft zone and tensile stress in the hard zone, ultimately achieving heterogeneity-induced (HDI) work hardening. This study is to EBM technology for the design and fabrication of three types of M2 high-speed steel samples, denoted as SS-1, SS-2, and SS-3, utilizing three distinct scanning strategies: single melting, double melting, and a combination thereof. The microstructure and phase evolution of these samples were comprehensively characterized using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron backscatter diffraction (EBSD) techniques. The findings demonstrate that when sample SS-3 was subjected to the combined scanning strategy involving both single melting and double melting approaches, its crystal structure exhibited a gradient distribution along with the presence of back stress during tensile testing. Sample SS-3 achieved an average tensile strength of 1479 MPa with an average elongation rate of 1.8%. This represents an enhancement in average tensile strength by approximately 8.6% compared to sample SS-1 (∼1362 MPa) and a significant increase in average elongation rate by around 20% compared to SS-1 (∼1.44%). The gradient grain structure materials show the microstructure transformation from fine grain to coarse-grain in the same material, thus reducing the stress concentration caused by the change of mechanical properties in each region. The SS-3 sample can maintain significant ductility while improving tensile strength. Consequently, this represents a pivotal direction for the advancement of high-performance structural materials. The conducted experimental studies have demonstrated that geometrically necessary dislocations (GNDs) and their associated strain hardening play a crucial role in enhancing the strength of grain structure materials. Additionally, these are essential to achieve an exceptional synergy between strength and toughness in these materials.

Influence of Cell Structure on Yield Strength and Strain‐Hardening Behavior in Additively Manufactured H13 Hot Work Tool Steel

High Strength (~2000 MPa) or Highly Ductile (~11%) Additively Manufactured H13 by Tempering at Different Conditions

Effect of Different Post-Processing Thermal Treatments on the Fracture Toughness and Tempering Resistance of Additively Manufactured H13 Hot-Work Tool Steel

Microstructures and Mechanical Properties of H13 Tool Steel Fabricated by Selective Laser Melting

High-speed manufacturing-driven strength-ductility improvement of H13 tool steel fabricated by selective laser melting

Tempering behavior of a direct laser deposited hot work tool steel: Influence of quenching on secondary hardening and microstructure

Experimental Characterization and Yield Strength Model for Process-Structure-Property of Selective Laser Melted 316L

Anisotropic Mechanical Behavior of Additive Manufactured AISI 316L Steel

Microstructure and High-Temperature Tensile Behavior of Modified H13 Steel with the Addition of Tungsten, Molybdenum, and Lowering of Chromium

Microstructural and Hardness Behavior of H13 Tool Steel Manufactured by Ultrasound-Assisted Laser-Directed Energy Deposition

Microstructure evolution and mechanical properties of H13 steel produced by Selective Electron Beam Melting

Process-Structure-Property Relationships of AISI H13 Tool Steel Processed with Selective Laser Melting

Additive Manufacturing of AISI H13 Tool Steel with Combinations of Higher Laser Power and Scan Speed: Microstructural and Mechanical Properties Insights

Selective laser melting of H13: microstructure and residual stress

Microstructure Evolution and Precipitation Strengthening Behaviour of Additively Manufactured High-speed Steels

Superior strength-ductility in laser aided additive manufactured high-strength steel by combination of intrinsic tempering and heat treatment

Submerged arc additive manufacturing (SAAM) of low-carbon steel: Effect of in-situ intrinsic heat treatment (IHT) on microstructure and mechanical properties

Effect of Heat Treatment on Microstructural Evolution, Mechanical Properties and Tribological Properties of H13 Steel Prepared Using Selective Laser Melting

Improvement of mechanical property of M2 high-speed steel with hetero-microstructure tailored via electron beam melting

Comparison of Softening Behavior and Abrasive Wear Resistance between Conventionally and Additively Manufactured Tool Steels

Microstructure and Tempering Softening Mechanism of Modified H13 Steel with the Addition of Tungsten, Molybdenum, and Lowering of Chromium