Abstract:Defects and morphology engineering is a serviceable strategy to boost the electrochemical energy conversion and storage performance of carbon-based materials. In this study, nitrogen/sulfur codoped carbon nanotubes (NS-CNTs) were first obtained via the pyrolysis of presynthesized polyaniline nanotubes with micelles composed of methyl orange and ferric chloride acting as the soft template. Furthermore, intrinsic carbon defects and mesopores were introduced to obtain etched NS-CNTs (ENS-CNTs) composites by ammonia etching. The rational combination of intrinsic/extrinsic defects and porous nanotube morphology features is beneficial to the oxygen reduction reaction (ORR) and sulfur reduction reaction (SRR) performances of the ENS-CNTs electrode. The coexistence of intrinsic carbon defects and extrinsic N/S dopants can create massive catalytically active sites for electrochemical processes, while the porous one-dimensional nanotube-like carbon framework is responsible for accessibility of catalytic active sites, species hosting, electrical conductivity, mass transport, and stability. Consequently, the ENS-CNTs-30 (where 30 represents the corresponding etching time in minutes) electrode for ORR displayed a high half-wave potential of 859 mV vs RHE, a diffusion limiting current density of 6.65 mA cm–2, admirable stability, and methanol tolerance. The solid Zn–air battery (ZAB) assembled with ENS-CNTs-30 as the active material for the air cathode revealed remarkable power density (137 mW cm–2) and specific capacity (1467.4 mAh g–1 Zn). Meanwhile, the ENS-CNTs-30 electrode for SRR also demonstrated ameliorative lithium–polysulfide (LiPS) trapping capability and Li2S deposition kinetics. The lithium–sulfur battery (LSB) with ENS-CNTs-30 as sulfur host material unfolded initial capacities of 1100 and 883 mAh g–1 at 0.2 and 2 C, respectively, and a capacity retention ratio of 82.0% after 200 cycles at 0.2 C. This work provides a feasible strategy for defects and morphology engineering of multifunctional carbon-based catalysts in electrochemical energy conversion and storage fields.

Intrinsic defects promote rapid conversion of polysulfides on carbon surface to achieve high rate performance

Quantitative defect regulation of heterostructures for sulfur catalysis toward fast and long lifespan lithium-sulfur batteries

Defect-riched prussian blue analogues with superior adsorption-catalysis toward lithium polysulfides for high performance lithium-sulfur batteries

Structurally optimized intrinsic defect carbon driven polysulfide reduction reaction for quantum dot sensitized solar cells

Promoting “strong Adsorption” and “fast Conversion” of Polysulfides in Li‐S Batteries Based on Conductive Sulfides Host with Hollow Prism Structure and Surface Defects

Phosphorization-Introduced Defect-Rich Phosphorus-Doped Co 3 O 4 with Propelling Adsorption–Catalysis Transformation of Polysulfide

Quantitatively regulating defects of 2D tungsten selenide to enhance catalytic ability for polysulfide conversion in a lithium sulfur battery

Intrinsic Carbon Defects in Nitrogen and Sulfur Doped Porous Carbon Nanotubes Accelerate Oxygen Reduction and Sulfur Reduction for Electrochemical Energy Conversion and Storage

Catalytic Boosting Bidirectional Polysulfide Redox using Co 0.85 Se/C Hollow Structure for High‐Performance Lithium‐Sulfur Batteries

Well-defined metal-N4 sites coordinated defective carbon as efficient electrocatalysts for high performance lithium–sulfur batteries

Pentagon Defects Accelerating Polysulfides Conversion Enabled High‐Performance Sodium–Sulfur Batteries

Dual‐Defect Engineering of Bidirectional Catalyst for High‐Performing Lithium‐Sulfur Batteries

Creating Edge Sites within the 2D Metal‐Organic Framework Boosts Redox Kinetics in Lithium–Sulfur Batteries

Two C-S bonds derived from carbons with different IG/ID values promote high sulfur loads and stable capacity storage

Manipulating Electrocatalytic Li 2 S Redox via Selective Dual‐Defect Engineering for Li–S Batteries

Ni0.85Se/NiSe2-C electrocatalyst with defect engineering and heterostructure for the multifunctional acceleration of lithium polysulfide conversion

Coupling highly dispersed Sb2S3 nanodots with nitrogen/sulfur dual-doped porous carbon nanosheets for efficient immobilization and catalysis of polysulfides conversion

Hollow and Porous N‐Doped Carbon Framework as Lithium‐Sulfur Battery Interlayer for Accelerating Polysulfide Redox Kinetics

A "Catalysis‐Immobilization‐Deposition" Stepwise Strategy toward Dynamic Equilibrium of Polysulfides Conversion and Diffusion in Lithium‐Sulfur Batteries

Efficient Co 0.85 Se-CNT sulfur cathode derived from strong catalyst-support interactions: Contribution of adsorption-catalysis mechanism to the redox kinetics of polysulfides

Electrocatalysis of polysulfide conversion by conductive RuO2 nano dots for lithium-sulfur batteries