Abstract:This study demonstrates the successful fabrication of near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia (1.5YSZ) ceramics using current-ramp flash (CRF) sintering technique. The process involved regulating Joule heating in the samples by fine-tuning the input power through an alternating current field (nominal current density: 50 mA·mm −2 ) within a 3-minute timeframe at a furnace temperature of 1100°C. This approach effectively enhanced grain size uniformity, which is crucial for preventing sample cracking associated with spontaneous tetragonal-to-monoclinic (T→M) phase transformation, thereby promoting densification with average relative densities exceeding 99%. The highest average fracture toughness of the 1.5YSZ samples was measured at 9.2 MPa·m 0.5 using the standardized single-edge pre-cracked beam method. This toughness is approximately double that of commonly used 3YSZ samples produced by CRF sintering, all of which exhibited comparable average grain sizes and relative densities. Additionally, the 1.5YSZ samples demonstrated nearly identical resistance to low-temperature degradation (LTD) compared to the 3YSZ samples after accelerated hydrothermal aging at 140°C for 15 hours, roughly equivalent to 60 years at 37°C. The reduced yttria concentration in 1.5YSZ facilitates T→M phase transformation at lower stress thresholds, enhancing toughness through increased crack shielding from a larger volume fraction of transformed grains. Furthermore, the uniform yttria distribution in 1.5YSZ, revealed by scanning transmission electron microscopy, compensates for the reduced tetragonal phase stability and contributes to improved LTD resistance. Notably, these exceptional properties were achieved at a furnace temperature 300°C lower and with a sintering duration several hours shorter than those of conventionally-sintered counterparts.

Controlled sintering and phase transformation of yttria-doped tetragonal zirconia polycrystal material

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

Study of Factors Influencing the Microstructure and Phase Content of Ultrafine Y-Tzp

Influence of yttria addition on the phase transformations of zirconia from zircon ore by carbothermal reduction process

Diffusionless Cubic-To-Tetragonal Phase-Transition And Microstructural Evolution In Sintered Zirconia Yttria Ceramics

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

Realizing near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia ceramics via current-ramp flash sintering

Influence of Sintering Temperatures on Material Properties and Corresponding Milling Machinability of Zirconia Ceramics

Phase and structural evolution of zirconolite ceramics prepared by solid-state reaction sintering

Stability properties and microstructure properties of microwave-sintered CeO2 doped zirconia ceramics

Investigation of material removal mechanisms and ductile-brittle transition zone of zirconia ceramics sintered at various temperatures

Tetragonal‐to‐Monoclinic Phase Transitions in Nanocrystalline Rare‐Earth‐Stabilized Zirconia Prepared by a Mild Hydrothermal Method

Fabrication of Pure T′ Phase YSZ Ceramics by Spark Plasma Sintering

Nano-scale Mechanical Behaviors and Material Removal Mechanisms of Zirconia Ceramics Sintered at Various Temperatures

Synthesis and thermal stability of zirconia and yttria-stabilized zirconia microspheres

Quantitative analysis of zirconia powder by rietveld method of X-ray diffraction

Microstructure and phase transformation behavior of Al2O3–ZrO2 under microwave sintering

Accelerated Aging in 3 mol%-Yttria-Stabilized Tetragonal Zirconia Ceramics Sintered in Reducing Conditions

An EXAFS Study of the Nanocrystalline Transformation of ZrO2:Y2O3(5%)

Thermophysical and mechanical properties of cubic, tetragonal and monoclinic ZrO2

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics