Enhanced mechanical properties and oxidation resistance in Ti-rich medium entropy alloy via Al 2 O 3 addition

Xiaoling Chen,Chenran Xu,Liyang Fang,Guanglong Xu,Lingwei Yang,Hongqun Tang,Yifang Ouyang,Xiaoma Tao

DOI: https://doi.org/10.1016/j.vacuum.2024.113928

IF: 4

2024-12-06

Vacuum

Abstract:Lightweight high/medium entropy alloys (H/MEAs) have attracted significant attention for their potential applications in lightweight high-temperature materials. Incorporation of oxides or oxygen atoms is an effective strategy for enhancing the mechanical and oxidation resistance performance of H/MEAs. Therefore, this work investigated the microstructure, phase compositions, mechanical properties, and oxidation resistance of Ti-V-Cr medium entropy alloys with varying Al 2 O 3 oxide content. The results showed a notable improvement in mechanical performance and enhanced oxidation resistance with the addition of Al 2 O 3 . The incorporation of Al 2 O 3 oxides contributed to fine grain strengthening, interstitial strengthening, phase separation and transformation, collectively enhancing performance of the alloy. The 0.6 wt.% Al 2 O 3 -added Ti-25V-15Cr alloy achieved a balance between strength and ductility, with a density of 5.111 g/cm 3 , a yield strength of 1371 MPa, and a plasticity exceeding 40%, even in the as-cast state. The 1.2 wt.% Al 2 O 3 alloy exhibited a high yield strength of 1471 MPa and plasticity over 15%. Additionally, the 0.6 wt.% Al 2 O 3 -added alloy displayed superior oxidation resistance at 700 °C. The incorporation of Al 2 O 3 did not change the oxidation mechanism of the Ti-25V-15Cr alloy but reduced the oxidation extent on the surface by forming oxides of the same type with varying morphologies.

materials science, multidisciplinary,physics, applied