Strain Hardening Behavior of Ti-Rich Light-Weight Medium Entropy Alloys with Excellent Strength and Plasticity Synergy

M.J. Kai,Y.J. Ma,X.T. Wang,L. Cheng,J.B. Hu,Y.Y. Hu,T.R. Xu,G.J. Li,X.K. Meng,Zhenhua Cao

DOI: https://doi.org/10.2139/ssrn.4387467

2023-01-01

Abstract:Body centered cubic (bcc) medium/high entropy alloys have gained much attention due to the high strength, but they usually suffer from poor plasticity. In this work, we have prepared a series of as-cast Tix(AlVCr)100-x medium entropy alloys with low density and systematically studied the effect of Ti content upon mechanical properties. With the increment of Ti content from 40 at.% to 80 at.%, the yield strength of the alloys greatly increased from 635 MPa to a maximum of 1204 MPa, and then decreased to 784 MPa, maintaining an excellent plasticity over 80%. Among these, the best combination of high strength and high uniform plastic strain was achieved in the as-cast Ti60(AlVCr)40 sample, with ~ 50 % increment in yield strength comparing with Ti40(AlVCr)60 sample, leading to a superior specific yield strength of 255 MPa/(g/cm3). The enhancement of strength is mainly attributed to the synergic effects of solid-solution and coherent nano-precipitation strengthening, while the dislocation dominates deformation mechanism involving dislocation pining and dislocation cells are responsible for the superb strain-hardening behavior. This work provides significant insights into the design of novel light-weight medium/high entropy alloys (LW-M/HEAs) with optimized strength and plasticity.